DENYL 66 5010 CB
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Vamp Tech |
| Trademark: | DENYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ffGE2c_DENYL-66-5010-CB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 66, 50% glass fiber reinforced, not Flame Retardant compound, very good mechanical properties, chemically bonded. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.55 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.20 | % | |
| Across Flow | 0.50 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 13500 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 195 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.5 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 12 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength | 55 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 250 | °C | ASTM D648A |
| Vicat Softening Temperature | 255 | °C | ASTM D1525 1 |
| RTI Elec | 140 | °C | UL 746 |
| RTI Imp | 140 | °C | UL 746 |
| RTI Str | 140 | °C | UL 746 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 280 | °C | |
| Mold Temperature | 100 | °C |
| Note Message | |
|---|---|
| 1 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVALEN® PH 51 T 40 | Plastcom | PP, Unspecified | SLOVALEN® |
| TIPPLEN® K 499 | MOL Petrochemicals Co. Ltd. | PP Impact Copolymer | TIPPLEN® |
| VECTRA® E115i | Celanese Corporation | LCP | VECTRA® |
| 3M™ Dyneon™ PTFE Compound TF 3311 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |
| Gallonprene® GP520-6012 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |