Borealis PP RF926MO

Category:	PP Random Copolymer , Polypropylene Random Copolymer
Manufacturer:	Borealis AG
Trademark:	Borealis PP
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	ffCuAU_Borealis-PP-RF926MO.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

RF926MO is a specially modified transparent polypropylene random copolymer with high meltflow. This grade is intended for injection blow stretch moulding (IBSM). and is designed for high-speed injection moulding and contains nucleating and demoulding additives.

Products moulded from this grade exhibit excellent transparency, very good organoleptic properties, high impact at ambient temperature, relatively high stiffness, and good demoulding and antistatic properties.

General Information
Additive	Nucleating agent Antistatic property demoulding
Features	Nucleated Rigidity, high Highlight Antistatic property Impact resistance, high Recyclable materials Workability, good Good sensory characteristics High liquidity Definition, high Good demoulding performance Random copolymer
Uses	Bottle Container
Appearance	Clear/transparent
Forms	Particle
Processing Method	Multiple injection molding Stretch blow molding

Physical	Nominal Value	Unit	Test Method
Density	0.905	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	20	g/10 min	ISO 1133
Molding Shrinkage	1.0 - 2.0	%

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (R-Scale)	82		ISO 2039-2

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	1150	MPa	ISO 527-2/1
Tensile Stress (Yield)	29.0	MPa	ISO 527-2/50
Tensile Strain (Yield)	11	%	ISO 527-2/50

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	6.0	kJ/m²	ISO 179/1eA

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature ¹(0.45 MPa, Unannealed)	80.0	°C	ISO 75-2/B

Optical	Nominal Value	Unit	Test Method
Haze	< 5.0	%	Internal method

Injection	Nominal Value	Unit
Processing (Melt) Temp	210 - 260	°C
Mold Temperature	30.0 - 40.0	°C
Injection Rate	Fast
Holding Pressure	20.0 - 50.0	MPa

Injection instructions
Blow pressure: 5 - 20 barReheat temperature: < 130 °CRF926MO can be processed on standard stretch blow moulding machines.

Note Message
1 .	Injection molded specimen

Resin Grade	Manufacturer	Category	Trademark
Royalite R71/920	Spartech Plastics	PC+ABS	Royalite
Borlink™ LE4244S	Borealis AG	PE, Unspecified	Borlink™
DENILUB Z 00U 23TFAr	Vamp Tech	PPA	DENILUB
LNP™ THERMOCOMP™ PF005S compound	SABIC Innovative Plastics	Nylon 6	LNP™ THERMOCOMP™
Durethan® BM 240 H3.0 000000	LANXESS GmbH	Nylon 6	Durethan®