Zytel® 73G30HSL NC010
| Category: | Nylon 6 , NYLON RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | febk2F_Zytel-73G30HSL-NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% Glass Reinforced, Heat Stabilized, Polyamide 6 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.36 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.60 | -- | % | |
| Flow | 0.20 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr, 2.00 mm | 6.3 | -- | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 1.9 | -- | % | |
| Viscosity Number | 150 | -- | cm³/g | ISO 307 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 961/30) | 230 | 150 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9500 | 6000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 190 | 120 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.5 | 6.0 | % | ISO 527-2 |
| Tensile Creep Modulus | ISO 899-1 | |||
| 1 hr | -- | 5500 | MPa | |
| 1000 hr | -- | 4600 | MPa | |
| Flexural Modulus 1 | 8500 | 5500 | MPa | ISO 178 |
| Flexural Stress 2 | 280 | 180 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 10 | 21 | kJ/m² | |
| 23°C | 16 | 23 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 80 | 80 | kJ/m² | |
| 23°C | 100 | 100 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -30°C | 10 | 11 | kJ/m² | |
| 23°C | 15 | 20 | kJ/m² | |
| Unnotched Izod Impact Strength (23°C) | 80 | -- | kJ/m² | ISO 180/1U |
| Multi-Axial Instrumented Impact Energy (23°C) | 3.50 | 6.50 | J | ISO 6603-2 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 220 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 210 | -- | °C | ISO 75-2/A |
| Glass Transition Temperature 3 | 65.0 | -- | °C | ISO 11357-2 |
| Vicat Softening Temperature | 215 | -- | °C | ISO 306/B50 |
| Melting Temperature 4 | 221 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 2.6E-5 | -- | cm/cm/°C | |
| Transverse | 7.5E-5 | -- | cm/cm/°C |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate (1.00 mm) | 50 | -- | mm/min | ISO 3795 |
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.750 mm | HB | -- | ||
| 1.50 mm | HB | -- | ||
| Oxygen Index | 21 | -- | % | ISO 4589-2 |
| Fill Analysis | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Melt Density | 1.20 | -- | g/cm³ | |
| Specific Heat Capacity of Melt | 2280 | -- | J/kg/°C | |
| Thermal Conductivity of Melt | 0.26 | -- | W/m/K |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Effective Thermal Diffusivity | 0.0910 | -- | cSt | |
| Emission of Organic Compounds | 8.50 | -- | µgC/g | VDA 277 |
| Note Message | |
|---|---|
| 1 . | PV |
| 2 . | PV |
| 3 . | 10°C/min |
| 4 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUPREME Specialty PS SP555 | Supreme Petrochem Ltd. | PS (IRPS) | SUPREME Specialty PS |
| TAROLOX 10 G5 | Taro Plast S.p.A. | PBT | TAROLOX |
| Kumho ABS HU600DS | Korea Kumho Petrochemical Co., Ltd. | ABS | Kumho ABS |
| Karina IVORY PVC COMPOUND 807D35/ 1-C-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Luran® S 777K | Styrolution | ASA | Luran® S |