Spartech Polycom SC2-1082
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | Spartech Polycom |
| Trademark: | Spartech |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fe1oZf_Spartech-Polycom-SC2-1082.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Spartech SC2-1082 is a soft flow high impact polystyrene (HIPS) resin for injection molding that is approved by the FDA. It also meets Underwriter's Laboratories requirements for 94 HB classification. HIPS are rubber modified styrenics that typically contain 1-10% rubber by weight. They offer dimensional and physical stability in moist environments and provide good chemical resistance. These materials also exhibit good flexibility along with good toughness. A very versatile product for a wide variety of applications, Spartech SC2-1082 is recommended for appliance, housewares, toys and electronic applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 6.5 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (23°C) | 20.7 | MPa | ASTM D638 |
| Flexural Modulus (23°C) | 2070 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 48.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed) | 78.9 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 82.2 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 200 - 220 | °C | |
| Middle Temperature | 205 - 225 | °C | |
| Front Temperature | 210 - 230 | °C | |
| Nozzle Temperature | 210 - 230 | °C | |
| Processing (Melt) Temp | 191 - 271 | °C | |
| Mold Temperature | 32.2 - 76.7 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® CLEAR G 830 Rnew | Arkema | Nylon Copolymer | Rilsan® |
| Nypol® PA A3 BRC0215 NR449 MSP | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| CALP E4331 | Lion Idemitsu Composites Co., Ltd. | Polyolefin, Unspecified | CALP |
| Karina WHITE PVC COMPOUND 805-10/127-A-ERYB-AS-PO | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 8220-65 Grey 9553 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |