CYCOLOY™ CY2010 resin
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | CYCOLOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fdG8u0_CYCOLOY-CY2010-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Flame retardant PC/ABS blend using non-brominated and non-chlorinated flame retardant systems, offering hydrolytic stability and excellent flow for a wide variety of thin wall or large size applications including business equipment, TV enclosures, among others |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/2.16 kg) | 31 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (260°C/2.16 kg) | 27.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 to 0.60 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.10 | % | |
| Equilibrium, 23°C, 50% RH | 0.050 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2800 | MPa | ASTM D638 |
| -- | 2670 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 65.0 | MPa | ASTM D638 |
| Yield | 63.0 | MPa | ISO 527-2/50 |
| Break 3 | 48.0 | MPa | ASTM D638 |
| Break | 43.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 3.9 | % | ASTM D638 |
| Yield | 3.5 | % | ISO 527-2/50 |
| Break 5 | 34 | % | ASTM D638 |
| Break | 40 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2630 | MPa | ASTM D790 |
| -- 7 | 2700 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 95.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 97.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9 | ISO 179/1eA | ||
| -30°C | 5.0 5.0 | kJ/m² | |
| 23°C | 10 | kJ/m² | |
| Charpy Unnotched Impact Strength 10 | ISO 179/1eU | ||
| -30°C | No Break No Break | ||
| 23°C | No Break No Break | ||
| Notched Izod Impact | |||
| -30°C | 69 | J/m | ASTM D256 |
| 23°C | 90 | J/m | ASTM D256 |
| -30°C 11 | 5.0 5.0 | kJ/m² | ISO 180/1A |
| 23°C 12 | 10 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 13 | ISO 180/1U | ||
| -30°C | No Break No Break | ||
| 23°C | No Break No Break | ||
| Instrumented Dart Impact (23°C, Total Energy) | 20.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 6.40 mm | 81.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 14 | 73.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 89.0 | °C | ISO 306/B50 |
| -- | 92.0 | °C | ISO 306/B120 |
| CLTE | ISO 11359-2 | ||
| Flow : -40 to 40°C | 7.5E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 7.5E-5 | cm/cm/°C |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.00 mm | V-2 | ||
| 1.50 mm | V-0 | ||
| Glow Wire Flammability Index (1.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.00 mm | 800 | °C | |
| 2.00 mm | 750 | °C | |
| 3.00 mm | 725 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Rear Temperature | 200 to 230 | °C | |
| Middle Temperature | 220 to 260 | °C | |
| Front Temperature | 230 to 270 | °C | |
| Nozzle Temperature | 220 to 260 | °C | |
| Processing (Melt) Temp | 230 to 270 | °C | |
| Mold Temperature | 50.0 to 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 sp=62mm |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 |
| 13 . | 80*10*4 |
| 14 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1399 X 128637 B | RTP Company | PPS | RTP |
| Ultradur® B 4300 M5 | BASF Corporation | PBT | Ultradur® |
| Karina WHITE PVC COMPOUND 800-10/177-Y-ERYB-PO | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ LUBRICOMP™ KP004 compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ LUBRICOMP™ |
| Panlite® AM-9730Z | TEIJIN LIMITED | PC+Polyester | Panlite® |