LNP™ THERMOCOMP™ MF002AS compound
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fdBzY0_LNP-THERMOCOMP-MF002AS-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* MF002AS is a compound based on Polypropylene resin containing 10% Glass Fiber. Added features of this material include: Heat Stabilized. Also known as: LNP* THERMOCOMP* Compound MF-1002 HS Product reorder name: MF002AS |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 0.958 | g/cm³ | |
| -- | 0.960 | g/cm³ | |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 1.0 to 3.0 | % | |
| Across Flow : 24 hr | 1.0 to 3.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.020 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.060 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3250 | MPa | ASTM D638 |
| -- | 2850 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 43.1 | MPa | ASTM D638 |
| Yield | 41.2 | MPa | ISO 527-2/5 |
| Break | 45.5 | MPa | ASTM D638 |
| Break 3 | 34.3 | MPa | ASTM D638 |
| Break | 35.4 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 3.5 | % | ASTM D638 |
| Yield | 3.4 | % | ISO 527-2/5 |
| Break | 3.7 | % | ASTM D638 |
| Break 5 | 5.5 | % | ASTM D638 |
| Break | 4.9 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2600 | MPa | ASTM D790 |
| -- | 2850 | MPa | ASTM D790 |
| -- 7 | 2380 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 68.9 | MPa | ASTM D790 |
| -- | 58.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 66.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 43 | J/m | ASTM D256 |
| 23°C 9 | 4.2 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 380 | J/m | ASTM D4812 |
| 23°C 10 | 25 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 8.50 | J | ASTM D3763 |
| -- | 2.20 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 146 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 11 | 122 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 105 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 74.0 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 7.6E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 1.1E-4 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 193 to 204 | °C | |
| Middle Temperature | 216 to 227 | °C | |
| Front Temperature | 238 to 249 | °C | |
| Processing (Melt) Temp | 227 to 249 | °C | |
| Mold Temperature | 32.2 to 48.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| 12 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 6035-55A | RTP Company | TPE | RTP |
| Syncure™ System S112NA | PolyOne Corporation | XLPE | Syncure™ |
| BESTNYL SE00VI01AS08 | Triesa Plastics | Nylon 66 | BESTNYL |
| GAPEX® HP RPP20EC07UL | Ferro Corporation | PP Homopolymer | GAPEX® HP |
| KumhoSunny PC 202 | Shanghai KumhoSunny Plastics Co., Ltd. | PC | KumhoSunny PC |