LNP™ THERMOCOMP™ LC006E compound
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fcmU42_LNP-THERMOCOMP-LC006E-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP* LC006E is a compound based on Polyetheretherketone resin containing Carbon Fiber. Added features of this material include: Easy Molding. Also known as: LNP* THERMOCOMP* Compound LC-1006 EM Product reorder name: LC006E |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.41 | g/cm³ | ISO 1183, ASTM D792 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.10 | % | ASTM D955 |
| Across Flow : 24 hr | 0.80 | % | ASTM D955 |
| Across Flow : 24 hr | 0.77 | % | ISO 294-4 |
| Flow : 24 hr | 0.11 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.060 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.10 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 25000 | MPa | ASTM D638 |
| -- | 24600 | MPa | ISO 527-2/1 |
| Tensile Strength (Break) | 228 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation | |||
| Break | 1.3 | % | ASTM D638 |
| Break | 1.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 21600 | MPa | ASTM D790 |
| -- | 21700 | MPa | ISO 178 |
| Flexural Strength | 340 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 64 | J/m | ASTM D256 |
| 23°C 2 | 6.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 430 | J/m | ASTM D4812 |
| 23°C 3 | 37 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 7.62 | J | ASTM D3763 |
| -- | 4.57 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 3.20 mm) | 300 | °C | ASTM D648 |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 1.8E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 3.4E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 349 to 360 | °C | |
| Middle Temperature | 366 to 377 | °C | |
| Front Temperature | 382 to 393 | °C | |
| Processing (Melt) Temp | 382 to 388 | °C | |
| Mold Temperature | 138 to 166 | °C | |
| Back Pressure | 0.344 to 0.689 | MPa | |
| Screw Speed | 60 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 299 A X 108950 H | RTP Company | Nylon 6 | RTP |
| Chemlon® A30 | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| Eltex® RSB 714 N0060 | INEOS Olefins & Polymers Europe | HDPE, HMW | Eltex® |
| LNP™ STAT-KON™ Noryl_NC2525 compound | SABIC Innovative Plastics | PPE+PS | LNP™ STAT-KON™ |
| Dryflex® V 85A101 | ELASTO | TPV | Dryflex® |