REPOL® C080MA
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | Reliance Industries Limited |
| Trademark: | REPOL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | faz68V_REPOL-C080MA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Repol C080MA is recommended for use in Injection Moulding processes where high impact strength is required. It is an ideal material to use in making furniture & industrial products. Repol C080MA contains antistatic agent that reduces static charge build-up in products. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, Injection Molded) | 23.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Yield, Injection Molded) | 7.0 | % | ASTM D638 |
| Flexural Modulus - 1% Secant (Injection Molded) | 1050 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, Injection Molded) | 150 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, Injection Molded) | 95.0 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | Type I, 50 mm/min |
| 2 . | Type I, 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2000 B-322 | RTP Company | PSU Alloy | RTP |
| Zythane® 6075A | Alliance Polymers & Services | TPU-Polyether | Zythane® |
| Bayblend® T45 PG | Covestro - Polycarbonates | PC+ABS | Bayblend® |
| Sylvin 8200-85 Grey 9568 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| SUMIMAC® ECR-9250K | SBHPP | Epoxy | SUMIMAC® |