Spartech SCR2-1087 is a high impact polystyrene (HIPS) resin for injection/extrusion molding applications. In addition to its high gloss characteristics, it also provides a good balance of toughness and rigidity. It also meets Underwriter's Laboratories requirements for 94 HB classification. HIPS are rubber modified styrenics that typically contain 1-10% rubber by weight. They offer dimensional and physical stability in moist environments and provide good chemical resistance. These materials also exhibit good flexibility along with good toughness. A very versatile product for a wide variety of applications, Spartech SCR2-1087 is recommended for appliances, housewares, toys, thermoformed and molded packaging, and custom sheet extrusion. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 4.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 - 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 25.2 | MPa | ASTM D638 |
| Flexural Modulus (23°C) | 2170 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 160 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed) | 91.1 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss (60°) | 80 | ASTM D523 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 82.2 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 200 - 220 | °C | |
| Middle Temperature | 205 - 225 | °C | |
| Front Temperature | 210 - 230 | °C | |
| Nozzle Temperature | 210 - 230 | °C | |
| Processing (Melt) Temp | 191 - 271 | °C | |
| Mold Temperature | 32.2 - 76.7 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X4785 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| RTP 2599 X 87260 C | RTP Company | PC+ABS | RTP |
| Moplen HP501D | Shazand (Arak) Petrochemical Corporation | PP Homopolymer | Moplen |
| UNICAR® SSFX02 | Nytef Plastics, Ltd. | PC | UNICAR® |
| ColorRx® FRA-1100NB | LTL Color Compounders, Inc. | ABS | ColorRx® |