Generic PP Homopolymer - Mineral
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | faDOdy_Generic-PP-Homopolymer---Mineral.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PP Homopolymer - Mineral This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.04 - 1.26 | g/cm³ | ASTM D792 |
| 23°C | 1.04 - 1.24 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 230°C/2.16 kg | 1.0 - 13 | g/10 min | ASTM D1238 |
| 230°C/2.16 kg | 1.7 - 21 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 10.4 - 18.1 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.20 - 1.3 | % | ASTM D955 |
| 23°C | 0.88 - 1.3 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 74 - 98 | ASTM D785 | |
| Durometer Hardness (23°C) | 72 - 79 | ISO 868 | |
| Ball Indentation Hardness | 77.5 - 100 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 2150 - 4100 | MPa | ASTM D638 |
| 23°C | 2140 - 4330 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 24.0 - 30.0 | MPa | ASTM D638 |
| Yield, 23°C | 24.4 - 34.4 | MPa | ISO 527-2 |
| Fracture, 23°C | 21.0 - 60.9 | MPa | ASTM D638 |
| Fracture, 23°C | 14.5 - 37.8 | MPa | ISO 527-2 |
| 23°C | 27.8 - 34.2 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield, 23°C | 3.7 - 4.4 | % | ASTM D638 |
| Yield, 23°C | 2.9 - 8.4 | % | ISO 527-2 |
| Fracture, 23°C | 3.0 - 51 | % | ASTM D638 |
| Fracture, 23°C | 1.1 - 100 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 1600 - 5800 | MPa | ASTM D790 |
| 23°C | 1740 - 4020 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 45.0 - 90.5 | MPa | ASTM D790 |
| 23°C | 41.3 - 59.1 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 1.3 - 4.2 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 20 - 51 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 24 - 51 | J/m | ASTM D256 |
| 23°C | 2.0 - 5.0 | kJ/m² | ISO 180 |
| Unnotched Izod Impact Strength (23°C) | 30 - 40 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 118 - 156 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 110 - 126 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 56.4 - 139 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 58.4 - 86.2 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 94.6 - 101 | °C | ASTM D1525 |
| -- | 81.3 - 158 | °C | ISO 306 |
| Melting Temperature (DSC) | 165 | °C | ISO 3146 |
| RTI Elec | 65.0 - 66.1 | °C | UL 746 |
| RTI Imp | 65.0 - 66.1 | °C | UL 746 |
| RTI | 65.0 - 66.1 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 7.5E+13 - 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+13 - 1.0E+15 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index | 955 - 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 744 - 750 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 85.0 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Rear Temperature | 205 - 211 | °C | |
| Middle Temperature | 200 - 213 | °C | |
| Front Temperature | 209 - 218 | °C | |
| Processing (Melt) Temp | 199 - 231 | °C | |
| Mold Temperature | 47.0 - 70.0 | °C | |
| Injection Pressure | 87.5 - 102 | MPa | |
| Back Pressure | 0.480 - 7.50 | MPa |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PP Homopolymer - MineralThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMTOUGH RZ300G6 | Polyram Ram-On Industries | PC | RAMTOUGH |
| Vi-Chem PVC V150-70 | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| Flontech® FT-1-FM-2 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| POLYFLAM® RPC 40400 | A. Schulman Europe | PC | POLYFLAM® |
| Sylvin 8950-90 Grey 9519 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |