Bapolene® PP5082
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | Bamberger Polymers, Inc. |
| Trademark: | Bapolene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fYa7bH_Bapolene-PP5082.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Bapolene PP 5082 is a multipurpose, high flow impact copolymer with excellent color and processability. This resin also exhibits a superior balance of stiffness and impact strength. This product meets the FDA requirements of 21CFR 177.1520. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.903 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 35 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 95 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 26.9 | MPa | ASTM D638 |
| Tensile Elongation 2(Yield) | 5.0 | % | ASTM D638 |
| Flexural Modulus - 1% Secant | 1240 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 98.9 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AKROMID® T1 GF 50 9 black (3257) | AKRO-PLASTIC GmbH | PPA | AKROMID® |
| Cri-Line HFLT-820 | Cri-Tech, Inc. | Fluorelastomer | Cri-Line |
| Durethan® BKV 30 000000 | LANXESS Corporation | Nylon 6 | Durethan® |
| Lionpol LC-60366 | Lion Polymers Incorporated | TPE | Lionpol |
| MAJORIS EE165 - 1791 | AD majoris | PP, Unspecified | MAJORIS |