Radilon® CA RV300L 100 NAT
| Category: | Nylon 66/6 , Polyamide 66/6 Copolymer |
| Manufacturer: | Radici Plastics |
| Trademark: | Radilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fV6b6Y_Radilon-CA-RV300L-100-NAT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PA66/6 copolymer injection moulding grade, 30% glass Fiber reinforced. Natural colour. Suitable for parts requiring high stiffness and good mechanical resistance. Good surface aspect and easier flow. ISO 1043 : PA66/6 GF30 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.28 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C, 2.00 mm | 7.0 | -- | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 1.7 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9500 | -- | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 170 | -- | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 4.1 | -- | % | ISO 527-2/1A/5 |
| Flexural Modulus 1 | 7600 | -- | MPa | ISO 178 |
| Flexural Stress 2 | 250 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 12 | -- | kJ/m² | |
| 23°C | 14 | -- | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 75 | -- | kJ/m² | |
| 23°C | 95 | -- | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 235 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 215 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 225 | -- | °C | ISO 306/B50 |
| Melting Temperature 3 | 245 | -- | °C | ISO 11357 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 550 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate | 0.0 | -- | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | -- | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 700 | -- | °C | IEC 60695-2-12 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 80.0 | °C | |
| Drying Time - Desiccant Dryer | 2.0 to 4.0 | hr | |
| Dew Point - Desiccant Dryer | < -20.0 | °C | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| 3M™ Dyneon™ Fluoroplastic FEP 6307Z | 3M Advanced Materials Division | FEP | 3M™ Dyneon™ Fluoroplastic |
| Daelim Po1y® PP-180 | DAELIM INDUSTRIAL CO., LTD. | PP Homopolymer | Daelim Po1y® |
| DINALON® PA 6 ESPECIAL IMPACTO MEDIO | Grupo Repol | Nylon 6 | DINALON® |
| Ketron® PEEK-GF30 LSG | Quadrant Engineering Plastic Products | PEEK | Ketron® |
| HiFill® TPX-IONOMER-02045 BK | Techmer Engineered Solutions | Ionomer | HiFill® |