LEXAN™ 505RU resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fRVo56_LEXAN505RUresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LEXAN 505RU is a 10% glass reinforced,flame retardant(FR)grade with non brominated and non chlorinated FR systems and UV stablization packages. This product is intended for applications to meet WEEE/RoHS regulations as well as various voluntary environmental labels. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.26 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 8.0 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 7.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 - 0.60 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.30 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.15 | % | ISO 62 |
| Outdoor Suitability | f1 | UL 746C |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3600 | MPa | ASTM D638 |
| -- | 3500 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 74.0 | MPa | ASTM D638 |
| Yield | 72.0 | MPa | ISO 527-2/5 |
| Fracture 3 | 62.0 | MPa | ASTM D638 |
| Fracture | 60.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 4.0 | % | ASTM D638 |
| Yield | 3.0 | % | ISO 527-2/5 |
| Fracture 5 | 6.0 | % | ASTM D638 |
| Fracture | 6.0 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 6 | 3200 | MPa | ASTM D790 |
| -- 7 | 3500 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 122 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 114 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9 | ISO 179/1eA | ||
| -30°C | 7.0 | kJ/m² | ISO 179/1eA |
| 23°C | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 10 | ISO 179/1eU | ||
| -30°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU | |
| Notched Izod Impact | |||
| -30°C | 70 | J/m | ASTM D256 |
| 23°C | 90 | J/m | ASTM D256 |
| -30°C 11 | 8.0 | kJ/m² | ISO 180/1A |
| 23°C 12 | 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1200 | J/m | ASTM D4812 |
| -30°C 13 | 73 | kJ/m² | ISO 180/1U |
| 23°C 14 | No Break | ISO 180/1U | |
| Instrumented Dart Impact (23°C, Total Energy) | 25.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 137 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 15 | 136 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 149 | °C | ASTM D1525, ISO 306/B120 11 16 |
| -- | 147 | °C | ISO 306/B50 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 5.0E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 7.4E-5 | cm/cm/°C | ASTM E831 |
| Lateral : -40 to 40°C | 8.5E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (CTI) | PLC 3 | UL 746 | |
| Comparative Tracking Index | 175 | V | IEC 60112 |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 3 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm, Testing by SABIC | V-2 | UL 94 | |
| 1.50 mm, Testing by SABIC | V-0 | UL 94 | |
| 3.00 mm, Testing by SABIC | 5VB 5VA | UL 94 | |
| Glow Wire Flammability Index (0.750 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.00 mm | 850 | °C | IEC 60695-2-13 |
| 3.00 mm | 875 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 60 | % | |
| Rear Temperature | 288 - 310 | °C | |
| Middle Temperature | 299 - 321 | °C | |
| Front Temperature | 310 - 332 | °C | |
| Nozzle Temperature | 304 - 327 | °C | |
| Processing (Melt) Temp | 310 - 332 | °C | |
| Mold Temperature | 82.2 - 116 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Vent Depth | 0.025 - 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | Type 1, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*3 sp=62mm |
| 10 . | 80*10*3 sp=62mm |
| 11 . | 80*10*3 |
| 12 . | 80*10*3 |
| 13 . | 80*10*3 |
| 14 . | 80*10*3 |
| 15 . | 80*10*4 mm |
| 16 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ecotan B FL HI 2 NERO | Soredi S.p.a. | Nylon 6 | Ecotan B |
| INSTRUC POMCGF30 | Infinity LTL Engineered Compounds | Acetal (POM) Copolymer | INSTRUC |
| Polifil® PP GFPPCC-40 | The Plastics Group | PP Homopolymer | Polifil® PP |
| ESTOPLAST XU 6242NN01 | Ester Industries Ltd. | Nylon 66 | ESTOPLAST XU |
| Sylvin 4200-88 Clear Green 3210 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |