TRIBOCOMP® PA66 GF40 TS5
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | EPIC Polymers |
| Trademark: | TRIBOCOMP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fQnVq6_TRIBOCOMP-PA66-GF40-TS5.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Tribosystem 5 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.56 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.30 | -- | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.2 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | ISO 527-2 | |||
| 23°C | 12500 | 9100 | MPa | ISO 527-2 |
| 120°C | 6500 | -- | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | |||
| Fracture, 23°C | 185 | 140 | MPa | ISO 527-2 |
| Fracture, 120°C | 95.0 | -- | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.4 | 3.8 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 11500 | 8200 | MPa | ISO 178 |
| Flexural Stress (23°C) | 255 | 210 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 12 | -- | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 48 | -- | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 252 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 250 | -- | °C | ISO 75-2/A |
| CLTE - Flow (23°C) | 2.7E-5 | -- | cm/cm/°C | ISO 7991 |
| Thermal Conductivity | 0.31 | -- | W/m/K | ISO 22007 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | -- | ohms | ASTM D257 |
| Dielectric Strength (2.00 mm) | 37 | -- | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 500 | -- | V | IEC 60112 |
| Additional Information |
|---|
| 干燥 The value listed as Molding Shrinkage ISO 294-4, was tested in accordance with S.O.P. methods. |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 270 - 300 | °C | |
| Middle Temperature | 275 - 295 | °C | |
| Front Temperature | 280 - 295 | °C | |
| Nozzle Temperature | 290 - 310 | °C | |
| Processing (Melt) Temp | < 300 | °C | |
| Mold Temperature | 80.0 - 130 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PureTherm® ESD 1500 | Tekni-Films, a div of Tekni-Plex | Film, PVC | PureTherm® |
| Sinvicomp SFW5060D | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| Sindustris PP SH5301 | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| BCC Resins MB5000 | BCC Products Inc. | PUR, Unspecified | BCC Resins |
| GAPEX® RPP20EB38AL | Ferro Corporation | PP Homopolymer | GAPEX® |