LUVOCOM®1850-8628 is a polybutene terephthalate (PBT) material containing carbon nanofillers. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. LUVOCOM®The main features of 1850-8628 are: flame retardant/rated flame Conductivity Electrostatic protection anti-warping Typical application areas include: Electrical/electronic applications House textile/fiber engineering/industrial accessories Automotive Industry

General Information
Filler / Reinforcement	Carbon nano filler
Features	Conductivity Low warpage Electrostatic discharge protection Antistatic property
Uses	Electrical/Electronic Applications Textile applications Engineering accessories Application in Automobile Field Business equipment Shell
Appearance	Black

Physical	Nominal Value	Unit	Test Method
Density	1.34	g/cm³	ISO 1183
Molding Shrinkage	1.4 - 2.0	%	DIN 16901
Water Absorption (23°C, 24 hr)	< 0.15	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	2800	MPa	ISO 527-2
Tensile Stress (Break)	52.0	MPa	ISO 527-2
Tensile Strain (Yield)	2.5	%	ISO 527-2
Flexural Modulus	2400	MPa	ISO 178
Flexural Stress	92.0	MPa	ISO 178
Flexural Strain at Flexural Strength	3.5	%	ISO 178

Thermal	Nominal Value	Unit	Test Method
Maximum operating temperature- Short Term	150	°C

Electrical	Nominal Value	Unit	Test Method
Insulation Resistance	1.0E+2	ohms	IEC 60167

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	88.0	°C	ISO 75-2/A
Continuous Use Temperature	130	°C	UL 746B

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	< 1.0E+5	ohms	IEC 60093

Flammability	Nominal Value	Unit	Test Method
Flame Rating ¹	HB		UL 94

Injection	Nominal Value	Unit
Drying Temperature
A	120	°C
Vacuum dryer, B	80.0	°C
Drying Time
A	4.0 - 6.0	hr
Vacuum dryer, B	6.0 - 8.0	hr
Suggested Max Moisture	0.020	%
Rear Temperature	240 - 260	°C
Middle Temperature	260 - 280	°C
Front Temperature	250 - 270	°C
Nozzle Temperature	250 - 265	°C
Processing (Melt) Temp	250	°C
Mold Temperature	60.0 - 120	°C

Injection instructions
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.02%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water very quickly, the predried material should be fed to the processing immediately. Processing temperatures above 270°C may very rapidly cause thermal damage and should therefore be avoided. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Injection instructions

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.02%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water very quickly, the predried material should be fed to the processing immediately. Processing temperatures above 270°C may very rapidly cause thermal damage and should therefore be avoided. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Note Message
1 .	Not recognized by UL.

Category:	PBT , Polybutylene Terephthalate
Manufacturer:	Lehmann & Voss & Co.
Trademark:	LUVOCOM®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	fQR4Z8_LUVOCOM-1850-8628.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Sinvicomp SRF3811	Teknor Apex Asia Pacific PTE. LTD.	PVC, Rigid	Sinvicomp
NEFTEKHIM PE 2062T (62107)	Nizhnekamskneftekhim Inc.	HDPE	NEFTEKHIM PE
4PROP® 9C12430	4Plas	PP Copolymer	4PROP®
Durethan® BKV 130 GIT DUS008 900116	LANXESS Corporation	Nylon 6	Durethan®
Techsil® RTV27905	Techsil Limited	Silicone Rubber, RTV-2	Techsil®