NYCOA NanoTUFF™ NT-90-100
| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | Nycoa (Nylon Corporation of America) |
| Trademark: | NYCOA NanoTUFF™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fQNngL_NYCOA-NanoTUFF-NT-90-100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NYCOA nanoTUFF™ NT - 90-100 is Nylon 6 based Nanocomposite with 10% clay loading made via in-situ polymerization for optimum nano-clay exfoliation. NYCOA nanoTUFF™ NT - 90-100 can be tailor-made to any specific viscosity range, depending upon the final application. This grade offers a 100% improvement in stiffness vs. neat Nylon 6, and is comparable in stiffness to a 20% glass-filled Nylon. In addition, barrier properties to water, oxygen, carbon dioxide, and fuel are improved approximately 80% vs. neat Nylon 6. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.16 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 51.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 2.0 | % | ASTM D638 |
| Flexural Modulus 3 | 5520 | MPa | ASTM D790 |
| Flexural Strength 4 | 140 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 27 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 155 | °C | ASTM D648 |
| Melting Temperature | 220 | °C | DSC |
| Additional Information |
|---|
| The value listed as Melting Point DSC, was tested in accordance with ASTM D789. |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| INEOS HDPE K38-20-188 | INEOS Olefins & Polymers USA | MDPE | INEOS HDPE |
| LNP™ LUBRICOMP™ OFL38A compound | SABIC Innovative Plastics Europe | PPS, Branched | LNP™ LUBRICOMP™ |
| MAJORIS DFR111R | AD majoris | PP, Unspecified | MAJORIS |
| Panlite® MN-4805Z | TEIJIN LIMITED | PC | Panlite® |
| NORYL™ WCD835 resin | SABIC Innovative Plastics | PPE+TPE | NORYL™ |