ADENE BXZB
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | A.D. Compound spa |
| Trademark: | ADENE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fPOquC_ADENE-BXZB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ADENE BXZB is a Polypropylene Homopolymer (PP Homopolymer) material filled with 50% calcium carbonate and 20% talc. It is available in Europe or North America for extrusion. Primary attribute of ADENE BXZB: Homopolymer. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.68 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.0 | g/10 min | ISO 1133 |
| Ash Content | 70 | % | ISO 3451-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 16.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 1.0 | % | |
| Break | 2.0 | % | |
| Flexural Modulus | 8300 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 3.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 88.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 110 | °C | ISO 306/B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| tefabloc® TP SD 310 80A | Mitsubishi Chemical Performance Polymers, Inc. | TPE | tefabloc® |
| TOTAL Polyethylene HDPE 5502 (EU) | TOTAL Refining & Chemicals | HDPE | TOTAL Polyethylene |
| UBE Polyamide Elastomer XPA 9048F1 | UBE Industries, Ltd. | TPA-ET | UBE Polyamide Elastomer |
| BJB Polyurethane TC-9460 A/B | BJB Enterprises, Inc. | TSU | BJB Polyurethane |
| ASTAMID™ MB3TUV | Marplex Australia Pty. Ltd. | Nylon 6 | ASTAMID™ |