NEXUS PS 536
| Category: | PS (GPPS) , General Purpose Polystyrene |
| Manufacturer: | Nexus Resin Group, LLC. |
| Trademark: | NEXUS PS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fOCrUz_NEXUS-PS-536.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
High Heat Flow Crystal Polystyrene in Injection Molding Nexus 536 is a high melt flow; high heat crystal polystyrene designed for fast cycle injection molding. This polymer is also designed for high output, direct injection profile extrusion for foam applications. Applications are for foam board and wood replacement. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 8.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 to 0.70 | % | ASTM D955 |
| Water Absorption (24 hr) | < 0.10 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2960 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 44.8 | MPa | ASTM D638 |
| Flexural Modulus | 2960 | MPa | ASTM D790 |
| Flexural Strength | 80.7 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Annealed) | 96.1 | °C | ASTM D648 |
| Vicat Softening Temperature | 104 | °C | ASTM D1525 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® LDPE 2801H0W | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |
| ACRYLITE® Resist ZK-F | Evonik Cyro LLC | Acrylic (PMMA) | ACRYLITE® |
| Borealis PP WH107AEB | Borealis AG | TPO | Borealis PP |
| EUROPLEX® Sheet PPSU 99470 KR Coating | Evonik Industries AG | PPSU | EUROPLEX® Sheet |
| Karina GREEN PVC COMPOUND -E810-40/312-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |