PREPERM® 260 LDS
| Category: | PPE , Polyphenylene Ether |
| Manufacturer: | Premix Oy |
| Trademark: | PREPERM® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fO3cXP_PREPERM-260-LDS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PREPERM® 260 LDS is a special compound based on polyphenylene ether (PPE). It is designed for laser direct structuring applications, such as mobile phone and other antennas, and circuitry. |
| General Information | |
|---|---|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.30 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/5.0 kg) | 13 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.80 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 62.0 | MPa | |
| 4.00 mm | 60.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 9.0 | % | |
| Break, 4.00 mm | 12 | % | |
| Flexural Modulus (4.00 mm) | 2800 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 1(23°C) | 12 | kJ/m² | ISO 180 |
| Unnotched Izod Impact Strength 2(23°C) | 45 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 177 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 158 | °C | ISO 75-2/Af |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Dielectric Constant (1.00 GHz) | 2.60 | Internal Method | |
| Dissipation Factor (1.00 GHz) | 5.0E-3 | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 140 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 290 to 310 | °C | |
| Mold Temperature | 80.0 to 140 | °C | |
| Injection Pressure | 60.0 to 80.0 | MPa | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 4 mm thickness |
| 2 . | 4 mm thickness |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Malen E FABS 23-D022 | LyondellBasell Industries | LDPE | Malen |
| Scolefin 34 G 10-8 | Ravago Group | PP Homopolymer | Scolefin |
| Vi-Chem PVC VNC50D-80I | Vi-Chem Corporation | PVC, Flexible | Vi-Chem PVC |
| New-prene™ 6050B | Total Polymer Vision (Suzhou) Co., LTD | PP+EPDM | New-prene™ |
| LNP™ LUBRICOMP™ SP003 compound | SABIC Innovative Plastics | Nylon 12 | LNP™ LUBRICOMP™ |