Vydyne® R535H NT651
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Ascend Performance Materials Operations LLC |
| Trademark: | Vydyne® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fO0u7W_Vydyne-R535H-NT651.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Vydyne R535H NT651 is a natural, 35% glass-filled PA66 resin. It is heat stabilized with an electrically neutral heat stabilizer and designed for electrical applications requiring high dielectric strength, low conductivity, and corrosion resistance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.41 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow : 2.00 mm | 0.90 | -- | % | |
| Flow : 2.00 mm | 0.40 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 0.80 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.6 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 11800 | 9500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 210 | 150 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | 2.9 | % | ISO 527-2 |
| Flexural Modulus | 10500 | 6000 | MPa | ISO 178 |
| Flexural Stress | 300 | 140 | MPa | ISO 178 |
| Poisson's Ratio | 0.40 | -- | ISO 527 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 11 | 11 | kJ/m² | |
| 23°C | 12 | 16 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 60 | 75 | kJ/m² | |
| 23°C | 68 | 89 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180 | |||
| -30°C | 12 | 12 | kJ/m² | |
| 23°C | 14 | 18 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 260 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 252 | -- | °C | ISO 75-2/A |
| Melting Temperature | 260 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 55°C | 1.9E-5 | -- | cm/cm/°C | |
| Transverse : 23 to 55°C | 7.5E-5 | -- | cm/cm/°C |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 280 to 310 | °C | |
| Middle Temperature | 280 to 310 | °C | |
| Front Temperature | 280 to 310 | °C | |
| Nozzle Temperature | 280 to 310 | °C | |
| Processing (Melt) Temp | 285 to 305 | °C | |
| Mold Temperature | 65.0 to 95.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULAMID® 66 MV HI TST | A. Schulman Europe | Nylon 66 | SCHULAMID® |
| Shandong PA6 A1G6301 | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon 6 | Shandong PA6 |
| Toyolac® 100-G10 | Toray Plastics (Malaysia) Sdn. Bhd. | ABS | Toyolac® |
| Bormed™ HE9601-PH | Borealis AG | HDPE | Bormed™ |
| Hanwha Total PP HJ730L | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |