BESTNYL SI25VI01BX
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Triesa Plastics |
| Trademark: | BESTNYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fNCKFn_BESTNYL-SI25VI01BX.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6 natural lubrified with 25% glass fibre reinforcement and V-0 quality, this material combines good mechanical properties and excellent flame resistance, generally employed in electrical industry or in final pieces that require V-0 quality. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.40 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.35 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 1.7 | % | ISO 62 |
| Ash Content | 25 | % | Internal Method |
| Humidity - Pellets | 0.20 | % | ISO 1110 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 79 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8700 | MPa | ISO 527-2 |
| Tensile Stress | 120 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 40 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 215 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 195 | °C | ISO 75-2/A |
| Vicat Softening Temperature | > 220 | °C | ISO 306 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Electric Strength | 22 | kV/mm | IEC 60243-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | < 100 | mm/min | FMVSS 302 |
| Flame Rating | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 220 to 230 | °C | |
| Mold Temperature | 50.0 to 60.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOLEN H031 BF | SIBUR, LLC | PP Homopolymer | TOLEN |
| Daelim Po1y® LH-641 | DAELIM INDUSTRIAL CO., LTD. | HDPE | Daelim Po1y® |
| Globalene® SI4101 | Lee Chang Yung Chemical Industry Corp. | PP Alloy | Globalene® |
| Karina ORANGE PVC COMPOUD 905-32/170-CY-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Polifil® Nylon 628-33GF | The Plastics Group | Nylon 66 | Polifil® Nylon |