Clariant Nylon 6/6 PA-131G33
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Clariant Corporation |
| Trademark: | Clariant Nylon 6/6 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fIUpKu_Clariant-Nylon-6-6-PA-131G33.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Clariant Nylon 6/6 PA-131G33 is a polyamide 66 (nylon 66) material, which contains a 33% glass fiber reinforced material. This product is available in North America and is processed by injection molding. The main features of Clariant Nylon 6/6 PA-131G33 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.32 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.70 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.80 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| Class m | 90 | ASTM D785 | |
| Class r | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 124 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 5520 | MPa | ASTM D790 |
| Flexural Strength | 179 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 170 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 238 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 204 | °C | ASTM D648 |
| CLTE - Flow | 3.6E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength | 22 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 266 - 293 | °C | |
| Middle Temperature | 266 - 293 | °C | |
| Front Temperature | 266 - 293 | °C | |
| Processing (Melt) Temp | 266 - 288 | °C | |
| Melt Temperature (Aim) | 274 | °C | |
| Mold Temperature | 65.6 - 93.3 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 20 - 100 | rpm | |
| Cushion | 3.18 - 6.35 | mm |
| Injection instructions |
|---|
| Injection Pressure: Use minimum pressure to achieve 95% fill during the boost inj. pressure phase.Hold Pressure: 30% to 75% of injection pressure.Mold Temp. Target: 180°FScrew Speed Target: 75 RPM |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prop 6002 | Putsch Kunststoffe GmbH | PP, Unspecified | Prop |
| RJM SE801G30 | RJM International, Inc. | AS | RJM |
| Expandable PS F21MB | INEOS Styrenics International SA | PS (EPS) | Expandable PS |
| Dryflex® 600500S | ELASTO | SEBS | Dryflex® |
| Plaslube® POM CO UV BK | Techmer Engineered Solutions | Acetal (POM) Copolymer | Plaslube® |