LNP™ LUBRICOMP™ DCP32 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fI2xZ9_LNP-LUBRICOMP-DCP32-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* LUBRICOMP* DCP32 is a compound based on Polycarbonate resin containing 15% PTFE/Silicone, 10% Carbon Fiber. Added features of this material include: Electrically Conductive, Wear Resistant. Also known as: LNP* LUBRICOMP* Compound DCL-4532 Product reorder name: DCP32 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.30 to 0.50 | % | ASTM D955 |
| Across Flow : 24 hr | 0.40 to 0.60 | % | ASTM D955 |
| Across Flow : 24 hr | 0.54 | % | ISO 294-4 |
| Flow : 24 hr | 0.43 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.10 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 7580 | MPa | ASTM D638 |
| -- | 7470 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 91.7 | MPa | ASTM D638 |
| Yield | 93.0 | MPa | ISO 527-2 |
| Break | 91.7 | MPa | ASTM D638 |
| Break | 93.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 2.1 | % | ASTM D638 |
| Yield | 2.2 | % | ISO 527-2 |
| Break | 2.1 | % | ASTM D638 |
| Break | 2.2 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 6210 | MPa | ASTM D790 |
| -- | 6700 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 138 | MPa | ASTM D790 |
| -- | 142 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.36 | ||
| vs. Itself - Static | 0.37 | ||
| Wear Factor - Washer | 49.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 91 | J/m | ASTM D256 |
| 23°C 2 | 9.1 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 440 | J/m | ASTM D4812 |
| 23°C 3 | 29 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 18.6 | J | ASTM D3763 |
| -- | 5.30 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 148 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 148 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 144 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 144 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 4.1E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 6.3E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| 4MID® 9A20000 | 4Plas | Nylon 66 | 4MID® |
| BP ABS 3333 R BLK | Buckeye Polymers, Inc. | ABS | BP |
| LEXAN™ SLX1432 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| PermaStat® 803 | RTP Company | Acetal (POM) Copolymer | PermaStat® |
| POCAN® DP C 1502 000000 | LANXESS Asia/Pacific | PC+PBT | POCAN® |