ElectriPlast® EP-SS/PC
| Category: | PC , Polycarbonate |
| Manufacturer: | Integral Technologies, Inc. |
| Trademark: | ElectriPlast® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fHlshZ_ElectriPlast-EP-SS-PC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ElectriPlast®EP-SS/PC is a polycarbonate (PC) product containing stainless steel fiber. It can be processed by injection molding and is available in North America. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.58 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4230 | MPa | ASTM D638 |
| Tensile Strength (Break) | 71.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 4120 | MPa | ASTM D790 |
| Flexural Strength | 120 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 56 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 410 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 136 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 25 | ohms | ESD STM11.11 |
| Volume Resistivity | 11 | ohms·cm | ASTM D257 |
| Static Decay | 10 | msec | Internal method |
| Surface Resistance | 2.0 | ohms | ESD STM11.11 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | < 17 | mm/min | UL 94 |
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 293 | °C | |
| Middle Temperature | 299 | °C | |
| Front Temperature | 304 | °C | |
| Nozzle Temperature | 299 | °C | |
| Mold Temperature | 93.3 | °C | |
| Back Pressure | 2.07 | MPa | |
| Screw Speed | 85 | rpm |
| Injection instructions |
|---|
| Injection Speed: 1 in/sec1st Stage (injection): 2400 psi2nd Stage (molding): 1000 psiDecomposition: 0.5 inch |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultramid® HFX 35 | BASF Corporation | Nylon 6 | Ultramid® |
| EPIMIX PBT CBR 20 NC | EPSAN Plastik SAN. ve TiC. A.S. | PBT | EPIMIX |
| IDI SMC S90 (Glass Content 30%) | IDI Composites International | TS, Unspecified | IDI SMC |
| Osterlene® CIE-9-00 | Osterman & Company | PS (GPPS) | Osterlene® |
| PERLER® O07U1000B11 | A.D. Compound S.p.A. | PP Copolymer | PERLER® |