Michiloy DM11100
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | API Polymers, Inc. |
| Trademark: | Michiloy |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fHAgrI_Michiloy-DM11100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Michiloy DM11100 is a Polycarbonate + ABS (PC+ABS) product. It is available in North America. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 2.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 52.4 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 100 | % | ASTM D638 |
| Flexural Modulus - Tangent | 2410 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 530 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 107 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.3 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 254 | °C | |
| Middle Temperature | 266 | °C | |
| Front Temperature | 271 | °C | |
| Nozzle Temperature | 271 | °C | |
| Processing (Melt) Temp | 288 | °C | |
| Mold Temperature | 87.8 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PrimoFlo 40A-300 | KMI Group Inc. | SEBS | PrimoFlo |
| Toraycon® 1200MF | Toray Plastics (Malaysia) Sdn. Bhd. | PBT | Toraycon® |
| Chemlon® AF413 | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| Ferro PP RPP30GT13UL NATURAL | Ferro Corporation | PP, Unspecified | Ferro PP |
| Lupox® TE5011 | LG Chem Ltd. | PC+PBT | Lupox® |