KetaSpire® KT-880SFP
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | KetaSpire® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fGrqTD_KetaSpire-KT-880SFP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
KetaSpire® KT-880SFP is the high flow grade of unreinforced polyetheretherketone (PEEK) supplied in a natural-color super-fine powder form. This super-fine PEEK powder is suitable for water borne coatings, electrostatically driven powder coatings, and resin pre-impregnation of continuous fiber composites. This super-fine powder is produced to a median particle size D50 of about 30 micrometers. KetaSpire® PEEK is produced to the highest industry standards and is characterized by a distinct combination of properties, which include excellent chemical resistance to acids, bases and a broad range of aggressive organic chemicals, best in class fatigue resistance, high thermal resistance, high purity and ease of melt processing. These properties make KT-880SFP well-suited for applications in health care, transportation, electronics, chemical processing and other industrial uses. The resin is also available in a natural-colored pellet form under the grade name KT-880 NT for injection molding applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Water Absorption (24 hr) | 0.10 | % | ASTM D570 |
| Particle Size | |||
| D50 | 30.0 | µm | |
| D90 | 55.0 | µm | |
| D99 | 120 | µm |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3650 | MPa | ASTM D638 |
| Tensile Strength | 100 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 5.2 | % | ASTM D638 |
| Fracture 1 | 10 - 20 | % | ASTM D638 |
| Flexural Modulus | 3790 | MPa | ASTM D790 |
| Flexural Strength | 153 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 53 | J/m | ASTM D256 |
| Unnotched Izod Impact | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 160 | °C | ASTM D648 |
| Glass Transition Temperature | 147 | °C | ASTM D3417 |
| Melting Temperature | 343 | °C | ASTM D3417 |
| CLTE - Flow (-50 to 50°C) | 5.0E-5 | cm/cm/°C | ASTM E831 |
| Injection instructions |
|---|
| Back Pressure: minimum |
| Note Message | |
|---|---|
| 1 . | Tensile test speed = 2 in/min (50 mm/min) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 6213-85 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Axiall PVC 18754 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Clariant Nylon 6/6 6604-L | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| Politen® G3TR20 | ITEN INDUSTRIES | Polyester Alloy | Politen® |
| VALOX™ PDR7904 resin | SABIC Innovative Plastics Asia Pacific | PBT | VALOX™ |