SABIC® PPcompound G3135X
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fGklNG_SABIC-PPcompound-G3135X.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PPcompound G3135X is a 35% short glass fiber reinforced Polypropylene. This material has been designed for high stiffness, high impact, high heat resistance and chemical resistance. The glass fibres are chemically coupled to the PP matrix. Typical application of this material would include air inlet manifolds. The material is available in standard black. SABIC® PPcompound G3135X is a designated automotive grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.17 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.0 | g/10 min | ISO 1133 |
| Molding Shrinkage (24 hr) | 0.40 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1A/5 | ||
| 23°C, 4.00 mm, Injection Molded | 7700 | MPa | |
| 80°C, 4.00 mm, Injection Molded | 4300 | MPa | |
| Tensile Stress (Break, 4.00 mm, Injection Molded) | 107 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break, 4.00 mm, Injection Molded) | 4.0 | % | ISO 527-2/1A/5 |
| Flexural Modulus 1(Injection Molded) | 8100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C, Injection Molded) | 15 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C, Injection Molded) | 60 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 160 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 152 | °C | ISO 75-2/A |
| Note Message | |
|---|---|
| 1 . | 3-point loading |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AMPLIFY™ TY 1057H | The Dow Chemical Company | MAH-g | AMPLIFY™ TY |
| apinat® DP2267 | API SpA | Biodeg Polymers | apinat® |
| DENKA ABS APG-3000 | Denka Company Limited | ABS | DENKA ABS |
| Kepamid® 1330M7 | Korea Engineering Plastics Co., Ltd | Nylon 6 | Kepamid® |
| LG ABS XR419 | LG Chem Ltd. | ABS | LG ABS |