NYCOA Polyamide 5100 HS
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Nycoa (Nylon Corporation of America) |
| Trademark: | NYCOA Polyamide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fGU1vy_NYCOA-Polyamide-5100-HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NYCOA 5100 HS is an impact modified, heat stabilized Nylon 66 resin used for injection molding. This material is specially formulated to provide improved flexibility and ductility vs standard Nylon 66. NYCOA 5100 HS offers outstanding toughness, exceptional processability, and a greater service life at elevated temperatures than standard grades of Nylon 66. It is available in UV stable, and custom colors grades. It also has excellent chemical resistance Typical applications include automotive wiring harnesses, motor component housings, gears, and electrical connectors. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.5 | % | ASTM D955 |
| Transverse flow | 1.6 | % | ASTM D955 |
| Water Absorption (24 hr) | 1.2 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 65.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 50 | % | ASTM D638 |
| Flexural Modulus 3 | 2220 | MPa | ASTM D790 |
| Flexural Strength 4 | 85.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (6.35 mm) | 140 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 189 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 65.0 | °C | ASTM D648 |
| Melting Temperature | 258 | °C | DSC |
| Additional Information |
|---|
| The value listed as Melting Point DSC, was tested in accordance with ASTM D789. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 82.2 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 249 - 266 | °C | |
| Middle Temperature | 266 - 277 | °C | |
| Front Temperature | 277 - 288 | °C | |
| Nozzle Temperature | 282 - 288 | °C | |
| Processing (Melt) Temp | 277 - 293 | °C | |
| Mold Temperature | 76.7 - 87.8 | °C | |
| Injection Rate | Fast | ||
| Back Pressure | 0.138 - 0.345 | MPa | |
| Cushion | 1.59 - 6.35 | mm | |
| Screw L/D Ratio | 16.0:1.0 | ||
| Screw Compression Ratio | 3.0:1.0 |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| 3 . | 51 mm/min |
| 4 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Melinex® 378 | DuPont Teijin Films U.S. | Polyester, TP | Melinex® |
| Durethan® BKV 50 H2.0 EF DUS030 901510 | LANXESS Corporation | Nylon 6 | Durethan® |
| Karina CLEAR PVC COMPOUND 80/204-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LUVOCOM® 1301-7629/EG | Lehmann & Voss & Co. | PPS, Linear | LUVOCOM® |
| Celstran® PP-GF30-04 Natural | Celanese Corporation | PP, Unspecified | Celstran® |