Retpol® CA 03 UVH
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | PolyPacific Pty. Ltd. |
| Trademark: | Retpol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fFgiL6_Retpol-CA-03-UVH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polycomp CA 03 UVH is an unfilled low to medium flow copolymer polypropylene compound. It is stabilized with a UV system designed for protection against extended outdoor exposure. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.898 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 1.5 to 1.9 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 3.00 mm) | 82 | ASTM D785 | |
| Durometer Hardness | ASTM D2240 | ||
| Shore D, 3.00 mm | 72 | ||
| Shore D, 15 sec, 3.00 mm | 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.00 mm) | 24.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.00 mm) | 500 | % | ASTM D638 |
| Flexural Modulus (3.00 mm) | 1130 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.00 mm) | 90 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.00 mm) | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 3.00 mm) | 90.0 | °C | ASTM D648 |
| CLTE - Flow (-30 to 30°C, 3.00 mm) | 1.0E-4 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Regrind | 10 | % | |
| Processing (Melt) Temp | 200 to 260 | °C | |
| Mold Temperature | 20.0 to 60.0 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Toyolac® 700 314 | Toray Plastics (Malaysia) Sdn. Bhd. | ABS | Toyolac® |
| DINAPLEN® PPH1S05 M203 | Grupo Repol | PP Homopolymer | DINAPLEN® |
| Expandable PS D833B | INEOS Styrenics International SA | PS (EPS) | Expandable PS |
| KOPA® KN135HB40BL | Kolon Plastics, Inc. | Nylon 6 | KOPA® |
| Karina BLUE COLOR CONCENTRATE 06/327-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |