COSMOPLENE® AZ191
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | TPC, The Polyolefin Company (Singapore) Pte Ltd |
| Trademark: | COSMOPLENE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fEuI7p_COSMOPLENEAZ191.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
COSMOPLENE AZ191 is a high impact PP copolymer manufactured by the latest gas phase process licensed from Sumitomo Chemical Co. Japan. It features a high impact property at high melt flow rate. COSMOPLENE AZ191 also shows good flowability and excellent surface appearance of parts after molding. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 30 | g/10 min | ASTM D1238 |
| Molding Shrinkage | Internal method | ||
| Flow : 2.00mm | 1.6 | % | Internal method |
| Transverse flow : 2.00mm | 1.6 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 66 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 21.0 | MPa | ASTM D638 |
| Fracture | 16.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 70 | % | ASTM D638 |
| Flexural Modulus | 940 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C | 82 | J/m | ASTM D256 |
| 23°C | 150 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 117 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 190 - 230 | °C | |
| Middle Temperature | 190 - 230 | °C | |
| Front Temperature | 190 - 230 | °C | |
| Mold Temperature | 30 | °C | |
| Injection Pressure | 6.86 | MPa | |
| Clamp Tonnage | 0.98 | kN/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUPREME HIPS SH825 | Supreme Petrochem Ltd. | PS (HIPS) | SUPREME HIPS |
| Unichem 8562 | Colorite Polymers | PVC, Unspecified | Unichem |
| 3M™ Dyneon™ TFM™ Modified PTFE TFM 1610 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ TFM™ Modified PTFE |
| Gallonprene® GP540-7005 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| GLAMIDE® T-521 | TOYOBO America, Inc. | Nylon 6 | GLAMIDE® |