Titacon® TX910
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Titan Plastics Compounds Co., Ltd. |
| Trademark: | Titacon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fDsxyn_Titacon-TX910.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Titacon®TX910 is a polyoxymethylene (POM) copolymer material,. This product is available in the Asia-Pacific region,. Titacon®The main features of TX910 are:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.38 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1(3.00 mm) | 1.7 - 2.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 50.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 45 | % | ISO 527-2 |
| Flexural Modulus | 1700 | MPa | ISO 178 |
| Flexural Stress | 65.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 14 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 87.0 | °C | ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 170 - 200 | °C | |
| Mold Temperature | 60.0 - 100 | °C |
| Injection instructions |
|---|
| Injection Pressure: 30 to 70%Injection Velocity: 20 to 50% |
| Note Message | |
|---|---|
| 1 . | 50x70x3 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Razamid® A111U | Razin™ Engineering Plastics | Nylon 66 | Razamid® |
| TAROMID B 280 G7 | Taro Plast S.p.A. | Nylon 6 | TAROMID B |
| YUNGSOX® PP 1005 | Formosa Polypropylene | PP Homopolymer | YUNGSOX® PP |
| BULKSAM® TM-30G6 | UMG ABS, Ltd. | ABS | BULKSAM® |
| Lifoflex® GB 1080 | Müller Kunststoffe GmbH | SEBS | Lifoflex® |