SABIC® LLDPE 726QJ

Category: LLDPE , Linear Low Density Polyethylene
Manufacturer: Saudi Basic Industries Corporation (SABIC)
Trademark: SABIC® LLDPE
Fillers: -
Ports: Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms FOB, CIF, DAP, DAT, DDP
PDF: fCMHEA_SABICLLDPE726QJ.pdf
PRICE: ​Order Products​ email   sales@su-jiao.com
Wechat: WECHAT
Message
SABIC® LLDPE 726QJ is a butene linear low density polyethylene resin. This grade is typically designed to give blown films a relatively high stiffness for good machinability and a good overall balance of other performance properties, such as puncture resistance, impact strength and heat sealability. This material contains anti block, slip erucamide and processing aid.

Application
Typical applications for SABIC® LLDPE 726QJ are shipping sacks, produce bags, can liners and carrier bags. SABIC® LLDPE 726QJ has good optical properties when blended with a LDPE (15-85%).

This product is not intended for and must not be used in any pharmaceutical/medical applications.
General Information
Additive
  • Processing aid
  • Erucamide Lubricating Additive
  • Anti-caking agent
  • Antioxidation
Features
  • Low density
  • Butene comonomer
  • Rigidity, high
  • smoothness
  • Perforation resistance
  • Anti-caking property
  • Antioxidation
  • Impact resistance, good
  • Machinable
  • Good heat sealability
  • Linear polymer structure
Uses
  • Blown Film
  • Films
  • Lining
  • Bags
Processing Method
  • Blow film
PhysicalNominal ValueUnitTest Method
Density 0.926g/cm³ISO 1183/A
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)0.70g/10 minISO 1133
MechanicalNominal ValueUnitTest Method
Coefficient of Friction (Blown Film)0.10ISO 8295
FilmsNominal ValueUnitTest Method
Film Thickness - Tested 50µm
Tensile Modulus ISO 527-3
    MD : 50 µm, blown film 220MPaISO 527-3
    TD : 50 µm, blown film 240MPaISO 527-3
Tensile Stress ISO 527-3
    MD : Yield, 50 µm, blown film 13.0MPaISO 527-3
    TD : Yield, 50 µm, blown film 14.0MPaISO 527-3
    MD : Broken, 50 µm, blown film 34.0MPaISO 527-3
    TD : Broken, 50 µm, blown film 27.0MPaISO 527-3
Tensile Elongation ISO 527-3
    MD : Broken, 50 µm, blown film 600%ISO 527-3
    TD : Broken, 50 µm, blown film 700%ISO 527-3
ImpactNominal ValueUnitTest Method
Impact Strength - Blown Film (50.0 µm) 230J/cmASTM D4272
Additional InformationNominal ValueUnitTest Method
Blocking - Blown Film (50.0 µm) 10gInternal method
Puncture Resistance - Blown Film (50.0 µm) 440J/mInternal method
Re-blocking - Blown Film (50.0 µm) gInternal method
Tear Strength 1ISO 6383-2
    MD : 50.0 µm 23.0kN/mISO 6383-2
    TD : 50.0 µm 130.0kN/mISO 6383-2
ThermalNominal ValueUnitTest Method
Vicat Softening Temperature 110°CISO 306/A
Melting Temperature (DSC) 124°CInternal method
OpticalNominal ValueUnitTest Method
Gloss (45°, 50.0 µm, Blown Film)65ASTM D2457
Haze (50.0 µm, Blown Film)14%ASTM D1003
Additional InformationNominal ValueUnitTest Method
Film of 50 µm and BUR=2 has been produced on Kiefel IBC with 130 kg/h. Die size 200 mm, die gap 0.8 mm.
Note Message
1 .Blown Film
Resin Grade Manufacturer Category Trademark
RJM EF401F1 RJM International, Inc. PPE+PS RJM
Nipoflex® 710 TOSOH Corporation EVA Nipoflex®
ACCUTECH™ HP0339C10L1 ACLO Compounders Inc. PP Homopolymer ACCUTECH™
CELEX™ 310HF.M Trinseo PC CELEX™
POLYFLAM® RIPP 2000 HI A. Schulman Europe PP Copolymer POLYFLAM®