CONATHANE® CE-1155
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | Cytec Industries Inc. |
| Trademark: | CONATHANE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | fAs1Ag_CONATHANE-CE-1155.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CONATHANE CE-1155 is a two-component, solvent-based polyurethane printed circuit board coating designed for use in adverse environments. CONATHANE CE-1155 provides outstanding resistance to moisture and good abrasion resistance. The cured film is hard and tough and has excellent adhesion to phenolic and epoxy-glass laminates. When tested over printed circuit patterns, excellent results are obtained with 1.5 mil films. Defective components can be replaced in coated areas using ordinary repair procedures without degradation or discoloration. Spot re-coating can then be accomplished. CONATHANE CE-1155 may be applied by spray, dip, or brush techniques and will cure at room or elevated temperatures. The cured film is suitable for continuous operation up to 130°C. The system contains a fluorescent dye to aid inspection under ultraviolet light. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- 1 | 0.958 | g/cm³ | |
| -- 2 | 1.13 | g/cm³ | |
| Solids Content | |||
| Hardener | 64 to 66 | % | |
| Resin | 60 | % | |
| Viscosity | Brookfield | ||
| Hardener : 25°C | 70 | mPa·s | |
| Resin : 25°C | 300 | mPa·s |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Pencil Hardness | HB |
| Flammability | Nominal Value | Unit | |
|---|---|---|---|
| Flash Point | |||
| Hardener | 7 | °C | |
| Resin | 27 | °C |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Fungal Resistance | Non-nutrient | ASTM G21 |
| Electrical | Nominal Value | Unit | |
|---|---|---|---|
| Surface Resistivity | 5.7E+14 | ohms | |
| Volume Resistivity (25°C) | 1.2E+16 | ohms·cm | |
| Dielectric Strength | |||
| 0.0508 mm | 120 | kV/mm | |
| 0.559 mm | 41 | kV/mm | |
| Dielectric Constant | |||
| 25°C, 100 Hz | 3.50 | ||
| 25°C, 1 kHz | 3.43 | ||
| 25°C, 1 MHz | 3.21 | ||
| Dissipation Factor | |||
| 25°C, 100 Hz | 0.014 | ||
| 25°C, 1 kHz | 0.014 | ||
| 25°C, 1 MHz | 0.016 | ||
| Insulation Resistance 3(25°C) | > 2.5E+13 | ohms |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 70 | ||
| Resin | Mix Ratio by Weight: 100 | ||
| Pot Life 4(25°C) | 360 | min | |
| Shelf Life (25°C) | 65 | wk | |
| Thermoset Mix Viscosity (25°C) | 72.0 | cP | ASTM D2393 |
| Demold Time (25°C) | 7200 to 10000 | min |
| Note Message | |
|---|---|
| 1 . | Hardener |
| 2 . | Resin |
| 3 . | Initially and 50% R.H. |
| 4 . | 400 Gram Mass |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Toler PP PP3530 | Toler Chemical, Inc | PP Impact Copolymer | Toler PP |
| AMTOPP SCP12 | Inteplast Group | PP, Unspecified | AMTOPP |
| Hanwha Total PP HF420 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP Homopolymer | Hanwha Total PP |
| Hifax TSOP EM1 G63083 | LyondellBasell Industries | PP Impact Copolymer | Hifax |
| TechnoFin PP T 10 | TechnoCompound GmbH | PP, Unspecified | TechnoFin |