Tarnamid® T- 27 TSL 4
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Grupa Azoty S.A. |
| Trademark: | Tarnamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | f9r5fw_Tarnamid-T--27-TSL-4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Impact modified. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 70.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 2.00 mm | 1.5 | % | |
| Flow : 2.00 mm | 2.0 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 9.5 | % | |
| Equilibrium, 23°C, 50% RH | 3.0 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 45.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 45.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 150 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 1600 | MPa | ISO 178 |
| Flexural Stress 2 | 50.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (-30°C) | 70 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 55.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 170 | °C | ISO 306/B |
| Melting Temperature | 221 | °C | ISO 11357-3 |
| Limit of Temperature - a few hours operation | < 160 | °C | |
| Temperature Index | |||
| 20000 hr | 70 | °C | |
| 5000 hr | 85 | °C |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ISO Type | PA6-HI, MR, 14020 | ISO 1874 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 80.0 | °C | |
| Suggested Max Moisture | < 0.10 | % | |
| Suggested Max Regrind | 50 | % | |
| Processing (Melt) Temp | 240 to 260 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Injection Pressure | 80.0 to 110 | MPa | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Carbotex K-20MRA | Kotec Corporation | PC | Carbotex |
| Fiberfil® J-62/30/E8 | Fiberfil® Engineered Plastics Inc. | PP Copolymer | Fiberfil® |
| Grivory® GVL-5H black 9839 | EMS-GRIVORY | Nylon 66+Nylon 6I/X | Grivory® |
| Isocor™ HZ73SI | Shakespeare Monofilaments and Specialty Polymers | Nylon 6 | Isocor™ |
| Karina COMP. PVC IVORY 80800-35/ 1-C-AC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |