LNP™ LUBRICOMP™ DFL32P compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | f9n42I_LNPLUBRICOMPDFL32Pcompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP DFL32P is a compound based on Polycarbonate resin containing 10% Glass Fiber, 15% PTFE. Added features include: Internally Lubricated, Exceptional Processing Also known as: LNP* LUBRICOMP* Compound DFL-4032 EP Product reorder name: DFL32P |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.36 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.20 - 0.50 | % | Internal method |
| Water Absorption (23°C, 24 hr) | 0.12 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4300 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield | 78.0 | MPa | ISO 527-2/5 |
| Fracture | 78.0 | MPa | ISO 527-2/5 |
| Tensile Strain | ISO 527-2/5 | ||
| Yield | 3.1 | % | ISO 527-2/5 |
| Fracture | 3.2 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 4700 | MPa | ISO 178 |
| Flexural Stress | 109 | MPa | ISO 178 |
| Coefficient of Friction (vs. Itself - Dynamic) | 0.41 | ASTM D3702 Modified | |
| Flexural Strain at Break 2 | 4.4 | % | ISO 178 |
| Wear Factor - Washer | 48.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 3(23°C) | 9.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 4(23°C) | 35 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 5 | |||
| 0.45 MPa, unannealed, 64.0mm span | 139 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64.0mm span | 133 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 4.6E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 7.4E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 - 304 | °C | |
| Middle Temperature | 310 - 321 | °C | |
| Front Temperature | 321 - 332 | °C | |
| Processing (Melt) Temp | 304 - 327 | °C | |
| Mold Temperature | 82.2 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2 mm/min |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Santoprene™ 203-50 | ExxonMobil Chemical | TPV | Santoprene™ |
| AIE PBT 30G3 | Asia International Enterprise (Hong Kong) Limited | PBT | AIE PBT |
| Boda FF2870 | Chenguang Fluoro & Silicone Elastomers Co., Ltd. | Fluorelastomer | Boda |
| Elastron® V V101.A90.B | Elastron USA, Inc. | TPV | Elastron® V |
| Plexiglas® Resist zk6BR | Evonik Industries AG | Acrylic (PMMA) | Plexiglas® |