GELOY™ FXW751SK resin
| Category: | ASA+PC , Acrylonitrile Styrene Acrylate + PC |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | GELOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | f9LUIt_GELOY-FXW751SK-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Sparkle Metallic VisualFx ASA+PC Resin - Weatherable, High Heat & Impact Resin |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.16 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 8.3 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 7.20 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 1.0 | % | |
| Equilibrium, 23°C, 50% RH | 0.25 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2690 | MPa | ASTM D638 |
| -- | 2900 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 62.0 | MPa | ASTM D638 |
| Yield | 60.2 | MPa | ISO 527-2/50 |
| Break 3 | 48.0 | MPa | ASTM D638 |
| Break | 48.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 4.2 | % | ASTM D638 |
| Yield | 4.2 | % | ISO 527-2/50 |
| Break 5 | 49 | % | ASTM D638 |
| Break | 77 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2750 | MPa | ASTM D790 |
| -- 7 | 2700 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 78.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 95.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 17 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 50 | J/m | ASTM D256 |
| 23°C | 170 | J/m | ASTM D256 |
| -30°C 10 | 5.2 | kJ/m² | ISO 180/1A |
| 23°C 11 | 17 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 43.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 89.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 93.5 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 105 | °C | ASTM D1525 13 |
| -- | 108 | °C | ISO 306/B50 |
| -- | 109 | °C | ISO 306/B120 |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 7.2E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 7.2E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.3 to 104 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Suggested Shot Size | 40 to 80 | % | |
| Rear Temperature | 238 to 254 | °C | |
| Middle Temperature | 243 to 260 | °C | |
| Front Temperature | 249 to 266 | °C | |
| Nozzle Temperature | 243 to 266 | °C | |
| Processing (Melt) Temp | 260 to 277 | °C | |
| Mold Temperature | 54.4 to 71.1 | °C | |
| Back Pressure | 0.345 to 1.03 | MPa | |
| Screw Speed | 30 to 80 | rpm | |
| Vent Depth | 0.038 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | Type I, 50 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYshine PBT D231 GF15 | Polykemi AB | PBT | POLYshine |
| Sinvicomp SIZ7408A | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| YUPLENE® H350F | SK Global Chemical | PP Homopolymer | YUPLENE® |
| HiFill FR® MPR 76A FR 1000 UV | Techmer Engineered Solutions | HDPE | HiFill FR® |
| Karina GRAY PVC COMPOUND 806-18/364-BY-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |