Cellophane™ 340XSC
| Category: | Cellulose, Regenerated , Regenerated Cellulose |
| Manufacturer: | Innovia Films Ltd. |
| Trademark: | Cellophane™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | f9FVD3_Cellophane-340XSC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Vinyl Coated Barrier Films for Packaging Applications Colored transparent general purpose 2 side PVdC coated, heat sealable, high barrier films. Literature reference: A105 |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic | 0.20 | ||
| vs. Itself - Static | 0.25 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 24 µm | > 3000 | MPa | |
| 1% Secant, TD : 24 µm | > 1500 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 24 µm | 125 | MPa | |
| TD : Yield, 24 µm | 70.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 24 µm | 22 | % | |
| TD : Break, 24 µm | 70 | % | |
| Seal Strength 1 | 1.6 | N/mm | Internal Method |
| Seal Initiation Temperature 2(24 µm) | 100 to 160 | °C | |
| Water Vapor Transmission Rate (24 µm, 38°C, 90% RH) | 10 | g·mm/m²/atm/24 hr | ASTM E96 |
| Film Gauge | 23.6 | µm | Internal Method |
| Yield (23.6 µm) | 29.4 | m²/kg | Internal Method |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gloss (45°, 23.6 µm) | 105 | ASTM D2457 |
| Note Message | |
|---|---|
| 1 . | 135°C; 0.5 secs; 69 kN/m 2 g(f)/38mm |
| 2 . | 0.5 sec dwell, 0.069 MN/m² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro-fax PD702 | LyondellBasell Industries | PP Homopolymer | Pro-fax |
| Radilon® A HS 2070 BIA 2758 | Radici Plastics | Nylon 66 | Radilon® |
| SIVIC® 2200 | SIDIAC | NBR | SIVIC® |
| GAPEX® HP RPP10EC14WH | Ferro Corporation | PP Homopolymer | GAPEX® HP |
| ESENTTIA 18H86 | Polipropileno del Caribe S.A. | PP Homopolymer | ESENTTIA |