AVP™ RLL10CP
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | AVP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | f6hNfk_AVP-RLL10CP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AVP™RLL10CP is a polycarbonate (PC) product that contains a 10% glass fiber reinforced material. It can be processed by injection molding and is available in North America. AVP™RLL10CP applications include electrical/electronic applications, electrical appliances and the automotive industry. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Recycled Content |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.30 - 0.50 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 3.18 mm) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3450 | MPa | ASTM D638 |
| Tensile Strength 1(Yield, 3.18 mm) | 56.5 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.18 mm) | 15 | % | ASTM D638 |
| Flexural Modulus 3(3.18 mm) | 3450 | MPa | ASTM D790 |
| Flexural Strength 4(3.18 mm) | 100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 64 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.35 mm) | 138 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.18 mm, BLK) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 | hr | |
| Drying Time, Maximum | 16 | hr | |
| Suggested Shot Size | 40 - 60 | % | |
| Rear Temperature | 282 - 293 | °C | |
| Middle Temperature | 288 - 316 | °C | |
| Front Temperature | 288 - 316 | °C | |
| Nozzle Temperature | 288 - 316 | °C | |
| Processing (Melt) Temp | 274 - 293 | °C | |
| Mold Temperature | 71.1 - 87.8 | °C | |
| Back Pressure | 0.345 - 1.38 | MPa | |
| Screw Speed | 40 - 70 | rpm |
| Note Message | |
|---|---|
| 1 . | 51 mm/min |
| 2 . | 51 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL PC-FD3-(color)-1 | Polymer Resources Ltd. | PC | PRL |
| Menzolit® BMC 1650 | Menzolit Ltd (UK) | Polyester, TS | Menzolit® |
| Chemlon® MDSF1 | Teknor Apex Company (Chem Polymer) | Nylon 6 | Chemlon® |
| Karina RED COLOR CONCENTRATE -E 42/183-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Pearlthane® 11T75D | Lubrizol Advanced Materials, Inc. | TPU-Capro | Pearlthane® |