Celcon® GC25TF
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Celanese Corporation |
| Trademark: | Celcon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | f6EfMu_Celcon-GC25TF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Celcon® GC25TF is a 25% glass coupled acetal copolymer formulated for higher flow in thin walled and small parts. Celcon GC25TF is also exceptionally resistant to fuel. It offers excellent resistance to transportation fuels especially oxygenated fuels. Chemical abbreviation according to ISO 1043-1: POM |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.58 | g/cm³ | ASTM D792 |
| -- | 1.57 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.40 | % | ASTM D955 |
| Transverse flow | 1.0 | % | ASTM D955 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.80 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8720 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Yield, 23°C | 117 | MPa | ASTM D638 |
| Fracture | 120 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2/1A/5, ISO 527-2/1A/50 |
| Flexural Modulus (23°C) | 8710 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.4 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 6.4 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, not annealed | 118 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 162 | °C | ISO 75-2/A |
| Melting Temperature | |||
| -- 1 | 165 | °C | ISO 11357-3 |
| -- | 166 | °C | ASTM D3418 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 3.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 170 - 180 | °C | |
| Middle Temperature | 180 - 190 | °C | |
| Front Temperature | 180 - 190 | °C | |
| Nozzle Temperature | 190 - 200 | °C | |
| Processing (Melt) Temp | 180 - 200 | °C | |
| Mold Temperature | 90.0 - 120 | °C | |
| Injection Pressure | 90.0 - 140 | MPa | |
| Injection Rate | Slow | ||
| Holding Pressure | 90.0 - 140 | MPa | |
| Back Pressure | 0.00 - 0.500 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 190 to 210°CZone 4 Temperature: 190 to 200°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLAN T-10W | POLYMA Kunststoff GmbH & Co. KG | ABS | POLYLAN |
| apigo® 9160 NL/90 | API SpA | TPO (POE) | apigo® |
| Celcon® MR25B | Celanese Corporation | Acetal (POM) Copolymer | Celcon® |
| Hanwha Total PE 310A | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | LDPE | Hanwha Total PE |
| EnviroTPO 2010T20 | West Michigan Compounding | Polyolefin, Unspecified | EnviroTPO |