TRIPPE® ST855HF
| Category: | PPE , Polyphenylene Ether |
| Manufacturer: | Samyang Corporation |
| Trademark: | TRIPPE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | f57cNx_TRIPPE-ST855HF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TRIPPE® ST855HF is a Polyphenylene Ether (PPE) product. It is available in Asia Pacific, Europe, or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 65 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.070 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 39.2 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 25 | % | ASTM D638 |
| Flexural Modulus | 2160 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 56.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 49 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 72.0 | °C | ASTM D648 |
| CLTE - Flow | 6.0E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-1 | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Megalon® 108ST | Mega Polymers | Nylon 66 | Megalon® |
| TECOLITE KM-13N(G) | KYOCERA Chemical Corporation | Phenolic | TECOLITE |
| DOWLEX™ 2107B | The Dow Chemical Company | LLDPE | DOWLEX™ |
| Karina WHITE PVC COMPOUND 653D10/ 1-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Optema™ TC 220 ExCo | ExxonMobil Chemical | EMA | Optema™ |