PRL PCSF-FRG20
| Category: | PC , Polycarbonate |
| Manufacturer: | Polymer Resources Ltd. |
| Trademark: | PRL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | f4vB1B_PRL-PCSF-FRG20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polymer Resources PCSF-FRG20 is a 20% glass fiber reinforced resin for structural foam molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 4.0 to 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.10 to 0.40 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 3.18 mm | 117 | MPa | |
| Break, 3.18 mm | 117 | MPa | |
| Flexural Modulus (3.18 mm) | 5170 | MPa | ASTM D790 |
| Flexural Strength (3.18 mm) | 124 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 149 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 141 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 129 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 293 to 316 | °C | |
| Middle Temperature | 304 to 327 | °C | |
| Front Temperature | 316 to 338 | °C | |
| Processing (Melt) Temp | 302 to 329 | °C | |
| Mold Temperature | 82.2 to 116 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Riteflex® 663HS | Celanese Corporation | TPC-ET | Riteflex® |
| COPYLENE® CM005 | Phillips 66 | PP Impact Copolymer | COPYLENE® |
| DynaStat® 157-SA | Polymer Dynamix | TPO | DynaStat® |
| Hostacom M2 R03 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Petrotene® PP A3 T40 PRTA011 PH376 MSP | Petropol Industry and Trade of Polymers LTDA | PP Homopolymer | Petrotene® PP |