RTP 6091-55A NATURAL
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | f4aZHR_RTP-6091-55A-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA-6 bondable - manufactured with Santoprene™ TPV technology |
| General Information | |
|---|---|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.930 | g/cm³ | ASTM D792 |
| Moisture Content | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 10 sec) | 55 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1(100% Strain, 3.18 mm) | 1.76 | MPa | ASTM D412 |
| Tensile Strength 2(Break, 3.20 mm) | 2.93 | MPa | ASTM D412 |
| Tensile Elongation 3(Break) | 300 | % | ASTM D412 |
| Tear Strength 4 | 11.4 | kN/m | ASTM D624 |
| Compression Set 5 | ASTM D395B | ||
| 70°C, 22 hr | 37 | % | ASTM D395B |
| 125°C, 22 hr | 56 | % | ASTM D395B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.10 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 263 - 282 | °C | |
| Mold Temperature | 35.0 - 71.1 | °C |
| Injection instructions |
|---|
| Desiccant Type Dryer Required. |
| Note Message | |
|---|---|
| 1 . | Mouth die C, 510mm/min |
| 2 . | C mold, 500 mm/min |
| 3 . | Mouth die C, 500 mm/min |
| 4 . | C mould |
| 5 . | Type 2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P1755 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Topolymer® 5211-951E | Dongguan Top Polymer Enterprise | TPE | Topolymer® |
| AEI SX538:CM540U | AEI Compounds Limited | XLPE | AEI |
| Andur 8500 AP/Curene® 442 | Anderson Development Company | PUR-Ether/TDI | Andur |
| Karina NATURAL PVC COMPOUND 70900-25/ 1-E-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |