EcoBlend® PAE9730
| Category: | ABS+PET , Acrylonitrile Butadiene Styrene + PET |
| Manufacturer: | Shanghai KumhoSunny Plastics Co., Ltd. |
| Trademark: | EcoBlend® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | f4Lp1U_EcoBlend-PAE9730.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PAE9730 is general purpose resin.PAE9730 is mainly used in ornament of small appliance, shell & panel of PC box,etc. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.15 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 240°C/5.0 kg | 15 | g/10 min | |
| 265°C/5.0 kg | 15 | g/10 min | |
| Molding Shrinkage - Flow | 0.60 to 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 50.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 40 | % | ASTM D638 |
| Flexural Modulus | 1850 | MPa | ASTM D790 |
| Flexural Strength | 65.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 400 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 80.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 100 | °C | ASTM D1525 1 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| CSA File No. | LS 66457 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 230 to 240 | °C | |
| Middle Temperature | 250 to 260 | °C | |
| Front Temperature | 265 to 275 | °C | |
| Nozzle Temperature | 260 to 270 | °C | |
| Processing (Melt) Temp | 265 to 275 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Back Pressure | 1.00 to 5.00 | MPa | |
| Screw Speed | 40 to 80 | rpm |
| Note Message | |
|---|---|
| 1 . | Rate B (120°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® PP HGZ-350SP | Saudi Polymers Company | PP Homopolymer | Marlex® PP |
| T-Blend® 5792N-PE | TSRC Corporation | TPE | T-Blend® |
| Karina BLACK PVC COMPOUND 750-48/1-GARAP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| HI-ZEX MILLION™ 630M | Mitsui Chemicals, Inc. | HMWPE | HI-ZEX MILLION™ |
| Tunhe PET TH102C | Xinjiang Blueridge Tunhe Chemical Industry Co.,Ltd | PET | Tunhe PET |