Di-Pak™ R-4525/30
| Category: | TP, Unspecified , Thermoplastic |
| Manufacturer: | Hapco Inc. |
| Trademark: | Di-Pak™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | f2GaYQ_Di-Pak-R-4525-30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
RIGID DI-PAK R-4525 Series A general purpose series of low viscosity, strong, potting and encapsulating compounds. DI-PAK R-4525 has excellent electrical insulating properties and bonds well to many substrates. By varying the curing agents, the desired cure and working life can be obtained. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.45 | g/cm³ | ASTM D4669 |
| Molding Shrinkage - Flow | 0.050 to 0.25 | % | ASTM D2566 |
| Weight - per cubic inch | 24 | g |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Service Temperature | 175 | °C |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gel Time 1(25°C) | 1.0 to 1.5 | hr | ASTM D2971 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 92 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2830 | MPa | ASTM D638 |
| Tensile Strength | 53.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 0.80 | % | ASTM D638 |
| Flexural Modulus | 3010 | MPa | ASTM D790 |
| Flexural Strength | 59.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 23 | J/m | ASTM D256 |
| Unnotched Izod Impact | 34 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Thermal Conductivity | 0.42 | W/m/K |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.2E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength | 2.5 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 1 kHz | 4.40 | ||
| 100 kHz | 4.20 | ||
| Dissipation Factor (25°C, 100 kHz) | 3.8E-3 | ASTM D150 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100, Mix Ratio by Volume: 100 | ||
| Part B | Mix Ratio by Weight: 15, Mix Ratio by Volume: 25 | ||
| Thermoset Mix Viscosity (25°C) | 11500 | cP | ASTM D4878 |
| Demold Time | |||
| 57°C | 120 to 240 | min | |
| 93°C | 120 to 240 | min |
| Note Message | |
|---|---|
| 1 . | 100 g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WELLAMID Nylon 6600 HW | CP-Polymer-Technik GmbH & Co. KG | Nylon 66 | WELLAMID Nylon |
| Xuchuan XWB-3310 | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Franprene TGA 2345LMO | Franplast S.r.l. | TPE | Franprene |
| EPLAMID 66 GX0 25 RP | EPSAN Plastik SAN. ve TiC. A.S. | Nylon 66 | EPLAMID 66 |
| ICORENE® N2801 | ICO Polymers EMEA, A Division of A. Schulman | HDPE | ICORENE® |