Order Products : sales@su-jiao.com
Chemraz 657
| Category: | Perfluoroelastomer , Perfluoroelastomer |
| Manufacturer: | Greene, Tweed & Co. |
| Trademark: | Chemraz |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | f29yYD_Chemraz-657.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Specifically developed to meet the demands of aggressive dry plasma systems, Chemraz® 657 perfluoroelastomer's unique formulation provides enhanced plasma resistance and minimal contamination resulting in less downtime and higher wafer processing yields. Recommended primarily for both static and dynamic oxide etch wafer processing applications, Chemraz 657 remains stable at service temperatures up to 280°C (536°F) with excursions to 300°C (572°F). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Specific Gravity | 2.03 | g/cm³ |
| Hardness | Nominal Value | Unit | |
|---|---|---|---|
| Durometer Hardness (Shore A) | 85 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 50% Strain | 4.45 | MPa | |
| 100% Strain | 9.55 | MPa | |
| Tensile Strength (Break) | 15.2 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 150 | % | ASTM D412 |
| Compression Set (96°C, 70 hr) | 29 | % | ASTM D395 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Service Temperature | -40 to 280 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vydyne® M344 BLK | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| Triapol® Blends F3 K28 UV NTLA010 BS307 | Petropol Industry and Trade of Polymers LTDA | PC+PBT | Triapol® Blends |
| Keltan® 9950C | LANXESS Buna GmbH | EPDM | Keltan® |
| Kumho SSBR SOL-C6270L | Korea Kumho Petrochemical Co., Ltd. | SBR, Solution | Kumho SSBR |
| REV Materials 8011-002 | REV Materials | PP, Unspecified | REV Materials |