TAROLON 2500 G4 X1
| Category: | PC , Polycarbonate |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROLON |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | f1uebZ_TAROLON-2500-G4-X1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polycarbonate medium viscosity, 20% glass fiber reinforced, self extinguishing UL94 V1, good mechanical properties also at high temperature, good dimensional stability. UL 94 V1 approved all colors at 1,6 mm and V0 at 3,5 mm. Available: in natural and opaque colors. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.33 to 1.35 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 12 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage - Flow | 0.30 to 0.50 | % | ASTM D955 |
| Water Absorption | |||
| 23°C, 24 hr | 0.080 | % | ASTM D570, ISO 62 |
| Saturation | 0.25 | % | ASTM D570 |
| Saturation, 23°C | 0.25 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6000 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Break) | 90.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 5500 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- 1 | 155 | MPa | ISO 178 |
| -- 2 | 145 | MPa | ISO 178 |
| Yield | 155 | MPa | ASTM D790 |
| Break | 145 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 3(23°C) | 9.0 | kJ/m² | ASTM D256, ISO 179 |
| Charpy Unnotched Impact Strength 4(23°C) | 42 | kJ/m² | ASTM D256, ISO 179 |
| Notched Izod Impact (23°C, 3.20 mm) | 130 | J/m | ISO 180, ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 142 | °C | ASTM D648, ISO 75-2/A |
| Continuous Use Temperature | |||
| -- | 80.0 | °C | UL 746B |
| -- 5 | 135 | °C | IEC 60216 |
| Vicat Softening Temperature | 153 | °C | ISO 306/A50, ASTM D1525 6 |
| Ball Pressure Test (135°C) | Pass | VDE 0470 | |
| CLTE - Flow (-30 to 30°C) | 3.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (2.00 mm) | 22 | kV/mm | ASTM D149 |
| Comparative Tracking Index (Solution A) | 175 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-1 | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 960 | °C | IEC 60695-2-13 |
| Oxygen Index | 31 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 100 to 110 | °C | |
| Pre-heater | 120 to 130 | °C | |
| Drying Time | |||
| -- | 1.0 to 2.0 | hr | |
| Pre-heater | 3.0 | hr | |
| Processing (Melt) Temp | 260 to 300 | °C | |
| Mold Temperature | 100 to 120 | °C | |
| Injection Rate | Fast |
| Note Message | |
|---|---|
| 1 . | Yield |
| 2 . | Break |
| 3 . | 6x4x50 mm |
| 4 . | 6x4x50 mm |
| 5 . | 20000 hrs |
| 6 . | Rate A (50°C/h), Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Small Boss SPVC2005 | Tongxiang Small Boss Special Plastic Products Co., Ltd. | PVC, Flexible | Small Boss |
| APEX® 3800-60NT1 | Teknor Apex Company | PVC, Flexible | APEX® |
| Evermore PUR SS-168K | Evermore Chemical Industry Co., Ltd. | PUR, Unspecified | Evermore PUR |
| PEXTIN™ PBT125-BK10 | Pier One Polymers, Inc. | PBT | PEXTIN™ |
| Plaslube® PPS GF40 TL13 | Techmer Engineered Solutions | PPS | Plaslube® |