LONGLITE® PMC T 399J
| Category: | Phenolic , Phenolic |
| Manufacturer: | CCP Group |
| Trademark: | LONGLITE® PMC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | f1uPce_LONGLITE-PMC-T-399J.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PMC T 399J is a glass fiber- and mineral-reinforced phenolic injection moulding compound |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.71 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | 0.50 | % | JIS K6915 |
| Water Absorption | |||
| 24 hr | 0.040 | % | ASTM D570 |
| 23°C, 24 hr | 0.040 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Strength | 160 | MPa | ASTM D790, ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 194 | °C | ASTM D648, ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.0E+11 | ohms | ASTM D257, IEC 60093 |
| Dielectric Strength (2.00 mm) | 17 | kV/mm | ASTM D149, IEC 60243-1 |
| Additional Information |
|---|
| Spiral Flow, CCP: 65 cmHeat Resistance, IEC 60216-P1, 2 hr: 210°CCharpy Impact, JIS K7111: 5.1 kg cm/cm² |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 60.0 - 95.0 | °C | |
| Middle Temperature | 60.0 - 95.0 | °C | |
| Front Temperature | 60.0 - 95.0 | °C | |
| Nozzle Temperature | 85.0 - 95.0 | °C | |
| Processing (Melt) Temp | 110 - 120 | °C | |
| Mold Temperature | 175 - 200 | °C | |
| Back Pressure | 0.800 - 1.00 | MPa |
| Injection instructions |
|---|
| Hardening Time: 45 sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Siloxane Masterbatch MB25-513 | Multibase, A Dow Corning Company | Siloxane, UHMW | Siloxane Masterbatch |
| SIBUR Synthetic Rubber SBR-1712 HI-AR Grade A | SIBUR, LLC | SBR, Unspecified | SIBUR Synthetic Rubber |
| Spartech Polycom SC7-7210R | Spartech Polycom | PC | Spartech |
| Cheng Yu VH826 | Cheng Yu Plastic Company Limited | ABS | Cheng Yu |
| Daelim Po1y® TR-570 | DAELIM INDUSTRIAL CO., LTD. | HDPE, HMW | Daelim Po1y® |