AKROMID® A3 1 natural (2416)
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | f1cLpx_AKROMID-A3-1-natural-2416-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® A3 1 natural (2416) is a heat stabilised, unreinforced polyamide 6.6 with light inherent color Applications are housings and fixtures in automotive and electric industry |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.14 | -- | g/cm³ | ISO 1183 |
| Spiral Flow | 104 | -- | cm | Internal Method |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 2.3 | -- | % | |
| Flow | 1.9 | -- | % | |
| Water Absorption (Saturation, 23°C) | 8.0 to 9.0 | -- | % | ISO 62 |
| Humidity Absorption - 62% RH (70°C) | 2.9 to 3.1 | -- | % | ISO 1110 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Temperature Index | IEC 216 | |||
| 50% Loss of Tensile Strength, 20000 hr | 100 to 120 | -- | °C | |
| 50% Loss of Tensile Strength, 5000 hr | 115 to 145 | -- | °C |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3200 | 1100 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 85.0 | 50.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | > 20 | > 50 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2800 | -- | MPa | ISO 178 |
| Flexural Stress 2 | 110 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 2.0 | 3.0 | kJ/m² | |
| 23°C | 5.0 | 13 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | No Break | ||
| 23°C | No Break | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 215 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 75.0 | -- | °C | ISO 75-2/A |
| Melting Temperature 3 | 262 | -- | °C | DIN EN 11357-1 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 80°C | 7.1E-5 | -- | cm/cm/°C | |
| Transverse : 23 to 80°C | 1.1E-4 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+13 | 1.0E+10 | ohms·cm | IEC 60093 |
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 4(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | V-2 | -- | UL 94 | |
| Glow Wire Flammability Index (1.60 mm) | 750 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (1.60 mm) | 675 | -- | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10 K/min, DSC |
| 4 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MarFlex® 5613 | Chevron Phillips Chemical Company LLC | LDPE | MarFlex® |
| 3M™ Dyneon™ PTFE Compound TF 2274 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE |
| Cri-Line FKX-719-75 | Cri-Tech, Inc. | Fluorelastomer | Cri-Line |
| Geon™ Vinyl Flexible B8000 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| IPC PP 4830H-T | International Polymers Corporation | PP Homopolymer | IPC PP |