SCHULAMID® 6 GF 20 FR GREY 96.7685 Datasheet,Nylon 6,A. Schulman Europe-SHANGHAI SUSHENG

Message
20% glass fibre reinforced flame-retardant Polyamide 6 grade (V-2); halogen free

General Information
Filler / Reinforcement	Glass fiber reinforced material, 20% filler by weight
Processing Method	Injection molding
Resin ID (ISO 1043)	PA 6 GF 20 FR(30)

Physical	Nominal Value	Unit	Test Method
Density	1.34	g/cm³	ISO 1183/A

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	4600	MPa	ISO 527-2/1A/1
Tensile Stress (Break)	60.0	MPa	ISO 527-2/1A/5
Tensile Strain (Break)	7.0	%	ISO 527-2/1A/5
Flexural Modulus	4000	MPa	ISO 178
Flexural Stress ¹			ISO 178
9.0% strain	95.0	MPa	ISO 178
3.5% strain	100	MPa	ISO 178
6.0% strain	105	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179/1eA
-30°C	4.0	kJ/m²	ISO 179/1eA
23°C	4.0	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength			ISO 179/1eU
-30°C	40	kJ/m²	ISO 179/1eU
23°C	50	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	205	°C	ISO 75-2/Bf
1.8 MPa, not annealed	140	°C	ISO 75-2/Af
Continuous Use Temperature ²	90.0	°C
Vicat Softening Temperature
--	215	°C	ISO 306/A50
--	205	°C	ISO 306/B50

Electrical	Nominal Value	Unit	Test Method
Dielectric Strength	35	kV/mm	IEC 60243-1
Comparative Tracking Index	450	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Flame Rating			UL 94, IEC 60695-11-10, -20
0.800 mm	V-2		UL 94, IEC 60695-11-10, -20
1.60 mm	V-2		UL 94, IEC 60695-11-10, -20
3.20 mm	V-2		UL 94, IEC 60695-11-10, -20
Glow Wire Flammability Index			IEC 60695-2-12
0.750 mm	960	°C	IEC 60695-2-12
1.50 mm	960	°C	IEC 60695-2-12
3.00 mm	960	°C	IEC 60695-2-12
Glow Wire Ignition Temperature			IEC 60695-2-13
0.750 mm	725	°C	IEC 60695-2-13
1.50 mm	725	°C	IEC 60695-2-13
3.00 mm	725	°C	IEC 60695-2-13

Additional Information
1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applicationsCharacteristic propertiesSCHULAMID 6 ... FR is the trade name of the halogen and (red) phosphorous free flame retardant Polyamide 6 grades.

Injection	Nominal Value	Unit
Drying Temperature	80.0	°C
Drying Time	3.0 - 4.0	hr
Suggested Max Moisture	0.040 - 0.10	%
Hopper Temperature	70.0	°C
Rear Temperature	230	°C
Middle Temperature	245	°C
Front Temperature	260	°C
Processing (Melt) Temp	< 260	°C
Mold Temperature	60.0 - 100	°C
Injection Pressure	80.0 - 140	MPa
Injection Rate	Moderate
Holding Pressure	40.0 - 85.0	MPa
Back Pressure	2.00 - 8.00	MPa
Screw Speed		mm/sec

Injection instructions
PredryingTypically a minimum predrying time of 3 to 4 hours at 80°C is recommended in a dehumidifying dryer. For optimal qualities a humidity of 0,04 - 0,1 % is recommended. Drying over 6 hours duration should occur at 60°C. Should be placed in the hopper.ReprocessingAddition of regrind is not recommended for nylons containing flame retardant.Shut downLong residence time should be avoided. Purge with polyolefin or with base polymer.FinishingThe material is suitable for machining. Varnishing, printing, gluing andembossing can be carried out using commercially available products.ConditioningRecently processed mouldings which not have been conditioned are brittle. The material picks up moisture until the equilibrium moisture content is reached. This may last for over a half year. Then the article has reached his balanced property profile. For accelerated absoption see our separate Technical instruction.RemarksFor permanent processing of glass fibre reinforced grades wear resistant screws and cylinders are recommended.

Injection instructions

PredryingTypically a minimum predrying time of 3 to 4 hours at 80°C is recommended in a dehumidifying dryer. For optimal qualities a humidity of 0,04 - 0,1 % is recommended. Drying over 6 hours duration should occur at 60°C. Should be placed in the hopper.ReprocessingAddition of regrind is not recommended for nylons containing flame retardant.Shut downLong residence time should be avoided. Purge with polyolefin or with base polymer.FinishingThe material is suitable for machining. Varnishing, printing, gluing andembossing can be carried out using commercially available products.ConditioningRecently processed mouldings which not have been conditioned are brittle. The material picks up moisture until the equilibrium moisture content is reached. This may last for over a half year. Then the article has reached his balanced property profile. For accelerated absoption see our separate Technical instruction.RemarksFor permanent processing of glass fibre reinforced grades wear resistant screws and cylinders are recommended.

Note Message
1 .	2.0 mm/min
2 .	Long periode (20000h)

Category:	Nylon 6 , Polyamide 6
Manufacturer:	A. Schulman Europe
Trademark:	SCHULAMID®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	f0Cmg0_SCHULAMID-6-GF-20-FR-GREY-96-7685.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
RTP 207 HS	RTP Company	Nylon 66	RTP
SILVER® SA-5324	Guangdong Silver Age Sci & Tech. Co., Ltd	Polyolefin, Unspecified	SILVER®
NOVALAC RX®626	Vyncolit N.V.	Phenolic	NOVALAC
Fainplast PVC CKL 86	Fainplast Compounds S.r.l	PVC, Unspecified	Fainplast PVC
Sylvin 5175-92 Yellow 4113	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin