Clyrell RC124H
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Clyrell |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ezoLFE_Clyrell-RC124H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Clyrell RC124H is a high modified polypropylene random copolymer designed for extrusion applications. Clyrell RC124H exhibits enhanced optical properties. The main applications of Clyrell RC124H are blown film extrusion, sheet extrusion and thermoforming. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 2.2 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 750 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 25.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 15 | % | |
| Break | 510 | % |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus | ASTM D882 | ||
| MD | 600 | MPa | |
| MD : 40 µm, Blown Film 1 | 840 | MPa | |
| TD : 40 µm, Blown Film 2 | 860 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield | 18.0 | MPa | |
| MD : Yield, 40 µm, Blown Film 3 | 27.0 | MPa | |
| TD : Yield, 40 µm, Blown Film 4 | 25.0 | MPa | |
| MD : Break | 40.0 | MPa | |
| MD : Break, 40 µm, Blown Film 5 | 31.0 | MPa | |
| TD : Break, 40 µm, Blown Film 6 | 27.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Yield, 40 µm, Blown Film 7 | 9.0 | % | |
| TD : Yield, 40 µm, Blown Film 8 | 8.0 | % | |
| MD : Break | 730 | % | |
| MD : Break, 40 µm, Blown Film 9 | 590 | % | |
| TD : Break, 40 µm, Blown Film 10 | 540 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 30 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 69.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 122 | °C | ISO 306/A50 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | ASTM D2457 | ||
| 45°, 50.0 µm | 91 | ||
| 45°, 40.0 µm, Blown Film | 93 | ||
| Haze | ASTM D1003 | ||
| 50.0 µm | < 1.0 | % | |
| 40.0 µm, Blown Film | 1.0 | % |
| Note Message | |
|---|---|
| 1 . | 25 mm/min |
| 2 . | 25 mm/min |
| 3 . | 500 mm/min |
| 4 . | 500 mm/min |
| 5 . | 500 mm/min |
| 6 . | 500 mm/min |
| 7 . | 500 mm/min |
| 8 . | 500 mm/min |
| 9 . | 500 mm/min |
| 10 . | 500 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALENE WPP121W | Southern Polymer, Inc. | PP Homopolymer | PRIMALENE |
| Nymax™ GF1200 A15 NC011 | PolyOne Corporation | Nylon 66 | Nymax™ |
| Formolene® DB5305A | Formosa Plastics Corporation, U.S.A. | UHMWPE | Formolene® |
| EPO-TEK® B9126-8 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| Guang Sung PVC GPMA95T | Guang Sung Plastics (GSPL) | PVC, Unspecified | Guang Sung PVC |